In this paper, highly ordered anodic aluminum oxide (AAO) template with hexagonal close-packed arrays was successfully fabricated through a two-step anodization process. Ag nanowire arrays with high aspect ratio were ...In this paper, highly ordered anodic aluminum oxide (AAO) template with hexagonal close-packed arrays was successfully fabricated through a two-step anodization process. Ag nanowire arrays with high aspect ratio were prepared using cyclic voltammetry within the confined nanochannels of AAO template. In addition, standing Ag nanowire arrays free-support of templates were also fabricated successfully by cyclic voltammetry method. The micrographs and crystal structures of Ag nanowires were studied by field emission scanning electron microscope (FESEM) and X-ray diffraction (XRD). FESEM observation showed that the Ag nanowire arrays with high aspect ratio lie orderly on the surface of the substrate. The diameter of the Ag nanowire is about 60 nm and the length up to 30 靘 or more. While the controlled nanowire arrays exhibit highly ordered structure in large area and the standing Ag nanowire in the array has the length of 1 靘 and good orientation. XRD results illustrated that the Ag nanowires in the arrays deposited by cyclic voltammetry method have a face centered cubic structure and are preferentially oriented in the (220) direction.展开更多
The macro- and micro-magnetic properties of Fe-Co alloy films eletrodeposited on CaAs（100） are studied by synchrotron radiation x-ray magnetic circular dichroism （XMCD） in combination with the magneto-optical Kerr...The macro- and micro-magnetic properties of Fe-Co alloy films eletrodeposited on CaAs（100） are studied by synchrotron radiation x-ray magnetic circular dichroism （XMCD） in combination with the magneto-optical Kerr effect （MOKE） measurements and magnetic force microscopy （MFM）. The orbital and spin magnetic moments of each element in the Fe-Co alloy are determined by the sum rules of XMCD. Element-specific hysteresis loops （ESHL） are obtained by recording the La MCD signals as a function of applied magnetic field. MOKE results reveal that the amorphous films are magnetically isotropic in the surface plane. The MFM image shows that the dimension of the magnetic domains is about 1-2 #m, which is much larger than that of the grains, indicating that there are intergranular correlations among these grains. Both ESHL and MOKE hysteresis loops indicate the strong ferromagnetic coupling of Fe and Co in the alloy films.展开更多
文摘In this paper, highly ordered anodic aluminum oxide (AAO) template with hexagonal close-packed arrays was successfully fabricated through a two-step anodization process. Ag nanowire arrays with high aspect ratio were prepared using cyclic voltammetry within the confined nanochannels of AAO template. In addition, standing Ag nanowire arrays free-support of templates were also fabricated successfully by cyclic voltammetry method. The micrographs and crystal structures of Ag nanowires were studied by field emission scanning electron microscope (FESEM) and X-ray diffraction (XRD). FESEM observation showed that the Ag nanowire arrays with high aspect ratio lie orderly on the surface of the substrate. The diameter of the Ag nanowire is about 60 nm and the length up to 30 靘 or more. While the controlled nanowire arrays exhibit highly ordered structure in large area and the standing Ag nanowire in the array has the length of 1 靘 and good orientation. XRD results illustrated that the Ag nanowires in the arrays deposited by cyclic voltammetry method have a face centered cubic structure and are preferentially oriented in the (220) direction.
基金Supported by the National Natural Science Foundation of China under Grant Nos 10274073 and 10505019.
文摘The macro- and micro-magnetic properties of Fe-Co alloy films eletrodeposited on CaAs（100） are studied by synchrotron radiation x-ray magnetic circular dichroism （XMCD） in combination with the magneto-optical Kerr effect （MOKE） measurements and magnetic force microscopy （MFM）. The orbital and spin magnetic moments of each element in the Fe-Co alloy are determined by the sum rules of XMCD. Element-specific hysteresis loops （ESHL） are obtained by recording the La MCD signals as a function of applied magnetic field. MOKE results reveal that the amorphous films are magnetically isotropic in the surface plane. The MFM image shows that the dimension of the magnetic domains is about 1-2 #m, which is much larger than that of the grains, indicating that there are intergranular correlations among these grains. Both ESHL and MOKE hysteresis loops indicate the strong ferromagnetic coupling of Fe and Co in the alloy films.