The microstructure and microhardness of Sn-3.5%Ag solders were explored in the cooling rate ranging from 0.08 to 104 K/s. Under rapid cooling condition, the strong kinetic undercooling effect leads to the actual solid...The microstructure and microhardness of Sn-3.5%Ag solders were explored in the cooling rate ranging from 0.08 to 104 K/s. Under rapid cooling condition, the strong kinetic undercooling effect leads to the actual solidification process starting at the temperature lower than the equilibrium eutectic point, and the actual metastable eutectic point shifts to the higher Ag concentration. Hence, the higher the applied cooling rate is, the more the volume fraction of primary β-Sn crystal forms. At the same time, the separation of primary β-Sn crystal favors restraining the formation of bulk Ag3Sn intermetallic compounds (IMCs) in solder due to the mismatch crystalline orientation relationship, those Ag3Sn phase separating through the eutectic reaction could hardly cling to the primary β-Sn crystal and grow up. Additionally, the Vickers hardness test shows that fine β-Sn and spherical Ag3Sn phase in the rapidly solidified alloy strongly improves the microhardness of the Sn-3.5%Ag solder.展开更多
基金Project(50401033) supported by the National Natural Science Foundation of China Project(200335) supported by the Foundation for the Author of National Excellent Doctoral Dissertation of China+1 种基金 Project(033608811) supported by the Natural Science Foundation of Tianjin City, China Project supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry
文摘The microstructure and microhardness of Sn-3.5%Ag solders were explored in the cooling rate ranging from 0.08 to 104 K/s. Under rapid cooling condition, the strong kinetic undercooling effect leads to the actual solidification process starting at the temperature lower than the equilibrium eutectic point, and the actual metastable eutectic point shifts to the higher Ag concentration. Hence, the higher the applied cooling rate is, the more the volume fraction of primary β-Sn crystal forms. At the same time, the separation of primary β-Sn crystal favors restraining the formation of bulk Ag3Sn intermetallic compounds (IMCs) in solder due to the mismatch crystalline orientation relationship, those Ag3Sn phase separating through the eutectic reaction could hardly cling to the primary β-Sn crystal and grow up. Additionally, the Vickers hardness test shows that fine β-Sn and spherical Ag3Sn phase in the rapidly solidified alloy strongly improves the microhardness of the Sn-3.5%Ag solder.