RESEARCH ON MATRIX CRACK EVOLUTION OF CROSS-PLY CERAMIC MATRIX COMPOSITE

The matrix crack evolution of cross-ply ceramic matrix composites under uniaxial tensile loading is investigated using the energy balance method.Under tensile loading,the cross-ply ceramic matrix composites have five damage modes.The cracking mode 3 contains transverse cracking,matrix cracking and fiber/matrix interface debonding.The cracking mode 5 only contains matrix cracking and fiber/matrix interface debonding.The cracking stress of modes 3 and 5 appearing between existing transverse cracks is determined.And the multiple matrix crack evolution of mode 3 is determined.The effects of ply thickness,fiber volume fraction,interface shear stress and interface debonding energy on the cracking stress and matrix crack evolution are analyzed.Results indicate that the cracking mode 3 is more likely to appear between transverse cracks for the SiC/CAS material.

双组元落压推进系统应用现状及关键技术

综述了国内外双组元落压推进系统的应用现状和技术特点,结合国内卫星推进系统的技术现状,分析了双组元落压推进系统混合比控制和大落压比高性能双组元发动机两个关键技术,提出了需开展氦气溶解特性、混合比变化、发动机偏工况试车等地面试验研究,为其工程应用提供技术支撑。

双组元落压推进系统混合比控制方法

双组元落压推进系统以其简单、高可靠、高比冲的特点在空间飞行器上逐渐得到应用。由于双组元落压推进系统压力和推进剂流量存在明显的变化,其混合比控制方法与双组元恒压推进系统存在显著的区别。本文分析了双组元落压推进系统混合比的影响因素,构建了混合比计算模型,提出了基于初始贮箱压力控制混合比的方法,并通过推进系统热试车验证了混合比控制方法的有效性。试验结果表明:通过控制初始贮箱压差不超过0.05 MPa,可将系统混合比偏差控制在不大于1.8%的指标范围内。

界面脱粘对正交铺设SiC/CAS复合材料基体开裂的影响

采用细观力学方法研究了正交铺设SiC/CAS复合材料在单轴拉伸载荷作用下界面脱粘对基体开裂的影响。采用断裂力学界面脱粘准则确定了0°铺层纤维/基体界面脱粘长度,结合能量平衡法得到了主裂纹且纤维/基体界面发生脱粘(即模式3)和次裂纹且纤维/基体界面发生脱粘(即模式5)的临界开裂应力,讨论了纤维/基体界面剪应力、界面脱粘能对基体开裂应力的影响。结果表明,模式3和模式5的基体开裂应力随纤维/基体界面剪应力、界面脱粘能的增加而增加。将这一结果与Chiang考虑界面脱粘对单向纤维增强陶瓷基复合材料初始基体开裂影响的试验研究结果进行对比表明,该变化趋势与单向SiC增强玻璃陶瓷基复合材料的试验研究结果一致。