单分子膜在水面上的聚集状态与膜分子的亲水基间的静电排斥作用和疏水基间Van der Waals引力的相对大小有关.在293K亚相温度下,2C_nSNa单分子膜聚集行为的电子显微研究表明,n=12时呈非晶性单分子膜;n=14时在较高的表面压下形成结晶性单...单分子膜在水面上的聚集状态与膜分子的亲水基间的静电排斥作用和疏水基间Van der Waals引力的相对大小有关.在293K亚相温度下,2C_nSNa单分子膜聚集行为的电子显微研究表明,n=12时呈非晶性单分子膜;n=14时在较高的表面压下形成结晶性单分子膜;n=16时可在表面压为0mN·m^(-1)的情况下形成结晶性单分子膜.FT-IR和透射电镜对单分子膜聚集结构的解析结果相互一致.本文还讨论了压缩速度对单分子膜π-A等温线的影响.展开更多
The PVC/EBBA ultrathin composite membranes with thickness of about 100 nm were prepared by spreading the solution on water surface. The overlapped composite membrane showed a characteristic aggregation structure in wh...The PVC/EBBA ultrathin composite membranes with thickness of about 100 nm were prepared by spreading the solution on water surface. The overlapped composite membrane showed a characteristic aggregation structure in which the polymer matrix exists as a three-dimensional spongy network and the liquid crystal domains werc observed. Tne surface modification for the overlapped membranes was carried out by means of plasma-polymerization with the monomers of fluorocarbon compounds. Both Arrhenius plots of permeability coefficients for oxygen ((?)_O_2) in the membrane samples before and after modification showed significant increase in the vicinity of the T_(KN) of EBBA.展开更多
Tapping mode atomic force microscope has been applied to observe single-chain PMMA particles which were stored for six months at room temperature after sprayed hom very dilute solutions in good solvents, good/poor mix...Tapping mode atomic force microscope has been applied to observe single-chain PMMA particles which were stored for six months at room temperature after sprayed hom very dilute solutions in good solvents, good/poor mixed solvents, and a theta solvent. Monodisperse PMMA standards of molecular weights ranging from 7.90 x 10(4) to 1.3 x 10(6) were used to investigate the effect of molecular weight on the size of the single-chain PMMA particles. These single-chain particles showed close to spherical shapes. The morphology of single-chain PMMA particles of a given molecular weight was found to be identical in spite of different solvents used for solution spraying. Molecular weight dependence of the particle dimension was also found. The diameters of single-chain PMMA particles after correction of tip-geometry effect were compared to the values estimated from molecular weight and density.展开更多
文摘单分子膜在水面上的聚集状态与膜分子的亲水基间的静电排斥作用和疏水基间Van der Waals引力的相对大小有关.在293K亚相温度下,2C_nSNa单分子膜聚集行为的电子显微研究表明,n=12时呈非晶性单分子膜;n=14时在较高的表面压下形成结晶性单分子膜;n=16时可在表面压为0mN·m^(-1)的情况下形成结晶性单分子膜.FT-IR和透射电镜对单分子膜聚集结构的解析结果相互一致.本文还讨论了压缩速度对单分子膜π-A等温线的影响.
基金Supported by the Science Fund of Academia Sinica and the National Natural Science Foundation of China
文摘The PVC/EBBA ultrathin composite membranes with thickness of about 100 nm were prepared by spreading the solution on water surface. The overlapped composite membrane showed a characteristic aggregation structure in which the polymer matrix exists as a three-dimensional spongy network and the liquid crystal domains werc observed. Tne surface modification for the overlapped membranes was carried out by means of plasma-polymerization with the monomers of fluorocarbon compounds. Both Arrhenius plots of permeability coefficients for oxygen ((?)_O_2) in the membrane samples before and after modification showed significant increase in the vicinity of the T_(KN) of EBBA.
基金This work was supported by The National Key Project for Fundamental Research"Macromolecular Condensed State".
文摘Tapping mode atomic force microscope has been applied to observe single-chain PMMA particles which were stored for six months at room temperature after sprayed hom very dilute solutions in good solvents, good/poor mixed solvents, and a theta solvent. Monodisperse PMMA standards of molecular weights ranging from 7.90 x 10(4) to 1.3 x 10(6) were used to investigate the effect of molecular weight on the size of the single-chain PMMA particles. These single-chain particles showed close to spherical shapes. The morphology of single-chain PMMA particles of a given molecular weight was found to be identical in spite of different solvents used for solution spraying. Molecular weight dependence of the particle dimension was also found. The diameters of single-chain PMMA particles after correction of tip-geometry effect were compared to the values estimated from molecular weight and density.