The spray-dried spheres within a W/Pt multi-separation can be used to prepare discrete core-shell WC@C/Pt catalysts through a typical carburization production mechanism at 800 ℃. In contrast with previous studies of ...The spray-dried spheres within a W/Pt multi-separation can be used to prepare discrete core-shell WC@C/Pt catalysts through a typical carburization production mechanism at 800 ℃. In contrast with previous studies of the WC/Pt synthesis, the reaction observed here proceeds through an indirect annealing thereby resulting in core-shell structure, and mechanism at 600℃ wherein species diffuse, Pt nanoparticles were successfully dispersed in size/shape and randomly scattered across the in situ produced C spheres. Through direct carburization or at higher initial hydrochloroplatiuic acid concentrations, however, complete reaction with core-shell spheres was not observed. Indirect carburization reduces the strain felt by the bonds featuring the larger WC WC and Pt nanoparticles to be reserved, stability toward methanol oxidation. particles and allows the motion of carbon around influencing the eleetrocatalytic performance and展开更多
基金This work is supported by the International Science ＆ Technology Cooperation Program of China（No.2010DFB63680）, the Natural Science Foundation of Zhejiang Province （LQ15B030004） and Loughborough University and the EPSRC （EP/1013229/1）.
文摘The spray-dried spheres within a W/Pt multi-separation can be used to prepare discrete core-shell WC@C/Pt catalysts through a typical carburization production mechanism at 800 ℃. In contrast with previous studies of the WC/Pt synthesis, the reaction observed here proceeds through an indirect annealing thereby resulting in core-shell structure, and mechanism at 600℃ wherein species diffuse, Pt nanoparticles were successfully dispersed in size/shape and randomly scattered across the in situ produced C spheres. Through direct carburization or at higher initial hydrochloroplatiuic acid concentrations, however, complete reaction with core-shell spheres was not observed. Indirect carburization reduces the strain felt by the bonds featuring the larger WC WC and Pt nanoparticles to be reserved, stability toward methanol oxidation. particles and allows the motion of carbon around influencing the eleetrocatalytic performance and