A series of materials Ce0.3+xZr0.6-xY0.1O1.95 were prepared by co-precipitation routine and the property of these materials was studied by means of oxygen storage capacity, temperature programming reduction, X-ray dif...A series of materials Ce0.3+xZr0.6-xY0.1O1.95 were prepared by co-precipitation routine and the property of these materials was studied by means of oxygen storage capacity, temperature programming reduction, X-ray diffraction, transmission electronic microscope, and X-ray photoelectron spectroscopy. The results indicate that the materials with a low Ce/Zr molar ratio possess higher cerium atom utilization ratio, reducibility and thermal stability than the materials with a high Ce/Zr ratio, and Ce0.35Zr0.55Y0.1O1.95 possesses the best properties.展开更多
The oxygen storage material (OSM) Ce0.35Zr0.55Y0.1O1.95 was prepared by co-precipitation routine and studied by means of TEM, XRD, XPS, BET, H2-TPR and oxygen storage capacity (OSC) measurements. The results indicated...The oxygen storage material (OSM) Ce0.35Zr0.55Y0.1O1.95 was prepared by co-precipitation routine and studied by means of TEM, XRD, XPS, BET, H2-TPR and oxygen storage capacity (OSC) measurements. The results indicated that this material possessed plenty of Ce3+ and lattice oxygen vacancy (percentage of Ce3+ was 59.6%) and high cerium atom utilization ratio (80.04%). The porous material was with an average BET surface area of 97 m2·g-1 and pore volume of 0.26 mL·g-1. After aged at 1 000 ℃ in air for 5 h, the sample still possessed plenty of Ce3+ and lattice oxygen vacancy (percentage of Ce3+ was 57.1%), and showed high cerium atom utilization ratio (78.25%), and high thermal stability.展开更多
Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (...Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (H2-TPR) after calcination at 100 ℃, 300 ℃, 600 ℃, and 1 000 ℃. The results showed that the precipitation was a crystalline of fluorite structure, and in the process of the precipitation transformation into Ce0.65Zr0.35O2 solid solution, the fluorite structure of the precipitation kept unchanged. The samples had different BET surface areas and OSC at different temperatures, but they held the performance of stable structure. After 1 000 ℃, there didn′t appear the other crystalline phase. So the samples prepared by co-precipitation method had excellent texture and higher thermal stability.展开更多
文摘A series of materials Ce0.3+xZr0.6-xY0.1O1.95 were prepared by co-precipitation routine and the property of these materials was studied by means of oxygen storage capacity, temperature programming reduction, X-ray diffraction, transmission electronic microscope, and X-ray photoelectron spectroscopy. The results indicate that the materials with a low Ce/Zr molar ratio possess higher cerium atom utilization ratio, reducibility and thermal stability than the materials with a high Ce/Zr ratio, and Ce0.35Zr0.55Y0.1O1.95 possesses the best properties.
文摘The oxygen storage material (OSM) Ce0.35Zr0.55Y0.1O1.95 was prepared by co-precipitation routine and studied by means of TEM, XRD, XPS, BET, H2-TPR and oxygen storage capacity (OSC) measurements. The results indicated that this material possessed plenty of Ce3+ and lattice oxygen vacancy (percentage of Ce3+ was 59.6%) and high cerium atom utilization ratio (80.04%). The porous material was with an average BET surface area of 97 m2·g-1 and pore volume of 0.26 mL·g-1. After aged at 1 000 ℃ in air for 5 h, the sample still possessed plenty of Ce3+ and lattice oxygen vacancy (percentage of Ce3+ was 57.1%), and showed high cerium atom utilization ratio (78.25%), and high thermal stability.
文摘Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (H2-TPR) after calcination at 100 ℃, 300 ℃, 600 ℃, and 1 000 ℃. The results showed that the precipitation was a crystalline of fluorite structure, and in the process of the precipitation transformation into Ce0.65Zr0.35O2 solid solution, the fluorite structure of the precipitation kept unchanged. The samples had different BET surface areas and OSC at different temperatures, but they held the performance of stable structure. After 1 000 ℃, there didn′t appear the other crystalline phase. So the samples prepared by co-precipitation method had excellent texture and higher thermal stability.