Indium doped zinc oxide （ZnO：In） thin films were prepared by ultrasonic spray pyrolysis on corning eagle 2000 glass substrate. 1 and 2 at.% indium doped single-layer ZnO：In thin films with different amounts of ace...Indium doped zinc oxide （ZnO：In） thin films were prepared by ultrasonic spray pyrolysis on corning eagle 2000 glass substrate. 1 and 2 at.% indium doped single-layer ZnO：In thin films with different amounts of acetic acid added in the initial solution were fabricated. The 1 at.% indium doped single-layers have triangle grains. The 2 at.% indium doped single-layer with 0.18 acetic acid adding has the resistivity of 6.82 × 10^-3 Ω. cm and particle grains. The doublelayers structure is designed to fabricate the ZnO：In thin film with low resistivity （2.58 × 10^-3 Ω. cm） and good surface morphology. It is found that the surface morphology of the double-layer ZnO：In film strongly depends on the substratelayer, and the second-layer plays a large part in the resistivity of the doublewlayer ZnO：In thin film. Both total and direct transmittances of the double-layer ZnO：In film are above 80% in the visible light region. Single junction a-Si：H solar cell based on the double-layer ZnO：In as front electrode is also investigated.展开更多
基金supported by Hi-Tech Research and Development Program of China (Grant Nos. 2007AA05Z436 and 2009AA050602)Science and Technology Support Project of Tianjin (Grant No. 08ZCKFGX03500)+3 种基金the National Basic Research Program of China (Grant Nos. 2011CB201605 and 2011CB201606)the National Natural Science Foundation of China (Grant No. 60976051)International Cooperation Project between China-Greece Government (Grant No. 2009DFA62580)Program for New Century Excellent Talents in University of China (Grant No. NCET-08-0295)
文摘Indium doped zinc oxide （ZnO：In） thin films were prepared by ultrasonic spray pyrolysis on corning eagle 2000 glass substrate. 1 and 2 at.% indium doped single-layer ZnO：In thin films with different amounts of acetic acid added in the initial solution were fabricated. The 1 at.% indium doped single-layers have triangle grains. The 2 at.% indium doped single-layer with 0.18 acetic acid adding has the resistivity of 6.82 × 10^-3 Ω. cm and particle grains. The doublelayers structure is designed to fabricate the ZnO：In thin film with low resistivity （2.58 × 10^-3 Ω. cm） and good surface morphology. It is found that the surface morphology of the double-layer ZnO：In film strongly depends on the substratelayer, and the second-layer plays a large part in the resistivity of the doublewlayer ZnO：In thin film. Both total and direct transmittances of the double-layer ZnO：In film are above 80% in the visible light region. Single junction a-Si：H solar cell based on the double-layer ZnO：In as front electrode is also investigated.