EIS studies the effect of Zinc to Al-Zn alloy used for cathodic protection in 3% NaCl solution

Electrochemical impendence spectroscopy （EIS） is applied to investigate the dissolution behavior of Al-Zn alloys in 3% NaCl solution at different polarization potentials. A new reaction model is proposed, and the activation mechanism of zinc in Al-Zn alloys is achieved. There are three intermediates in the dissolution process： Znad^＋, Znad^2＋ and Alad^＋, ,of which only Zni can activate Al-Zn alloys. Most Znnd^＋ is produced by β-phase,and the alloys with 2. 3% - 3. 8% （wt） Zn dissolve rapidly. The Al-Zn alloys of heart-shaped EIS are active in 3% NaCl solution, thus EIS characteristic can be used to distinguish the activa-tion of Al-Zn alloys.

铟含量对铝锌铟合金在3%NaCl溶液中溶解性能的影响

铟是活化铝的重要元素。通过测定铝锌铟合金试样在质量分数为3%的Na Cl溶液中不同阳极极化电位、不同表面状态下的EIS,分析铝锌铟合金的溶解行为,完善传统的溶解—沉积—再溶解机理,研究铟活化铝的作用。实验发现,随着铟含量的增加,Al-Zn-In合金开路电位降低,阻抗幅值减小,高In含量试样的溶解更快。结果表明,In的存在与否对Al-Zn-In合金溶解的影响显著。In的活化能力比较强,加入In后合金溶解的离子可以与穿透合金表面油膜的微量水分子反应,生成H_2。H_2可以撕裂表面油膜,进一步活化合金。

金属阳离子对镁在含Cl^-溶液中腐蚀行为的影响

采用动电位极化曲线、电化学阻抗谱(EIS)、失重腐蚀速率测试、扫描电镜(SEM/EDS)等分析方法对比研究了不同种类的金属阳离子(Na+,Ca^(2+),Mn^(2+))对镁腐蚀行为的影响。结果表明,金属阳离子类型对镁的腐蚀溶解速率有直接影响,腐蚀速率由大到小依次为Na+,Ca^(2+),Mn^(2+).这可能是由于较硬的金属阳离子(Ca^(2+),Mn^(2+))更容易渗入镁而改变膜层结构,形成更加均一致密的腐蚀产物膜,从而减缓镁腐蚀溶解进程。实验结果与软硬酸碱理论分析结果一致。