The high temperature oxidation behavior of Al Si coatings on the Ni base superalloy DZ125, with and without the ambient temperature corrosion test, was investigated. The results show that the isothermal oxidation beha...The high temperature oxidation behavior of Al Si coatings on the Ni base superalloy DZ125, with and without the ambient temperature corrosion test, was investigated. The results show that the isothermal oxidation behavior of the corroded coating changes, which has the higher mass gain than that of the original coating during the initial oxidation stage. Moreover, the cyclic oxidation resistance of the corroded coating decreases severely. The oxide scale was primarily composed of Al 2O 3, contaminated ...展开更多
基金Aeronautical Science Foundation of China(0 1I5 10 0 6)
文摘The high temperature oxidation behavior of Al Si coatings on the Ni base superalloy DZ125, with and without the ambient temperature corrosion test, was investigated. The results show that the isothermal oxidation behavior of the corroded coating changes, which has the higher mass gain than that of the original coating during the initial oxidation stage. Moreover, the cyclic oxidation resistance of the corroded coating decreases severely. The oxide scale was primarily composed of Al 2O 3, contaminated ...