In this paper a polyaluminum chloride solution with high Al13 content was prepared and used as raw material for preparation ofγ-Al2O3.The texture and crystalline phase of the prepared alumina samples were characteriz...In this paper a polyaluminum chloride solution with high Al13 content was prepared and used as raw material for preparation ofγ-Al2O3.The texture and crystalline phase of the prepared alumina samples were characterized by energy dispersive X-ray spectroscopy(EDX) ,X-ray diffraction,transmission electron microscope(TEM) and nuclear magnetic resonance(NMR) analyses.The effects of alkaline solution and calcination temperature were investigated.The results showed that alkaline solution including NH3·H2O and NaOH had little effect on the alumina sample formation.The impurities of NH4Cl and NaCl in solution can be removed through repeated washing by EDX analysis.Calcination temperature had a significant effect on alumina crystal phase.The alumina sample can transform completely toγ-Al2O3 in the subsequent heating from 600°C to 800°C.It is very interesting that Al13 can be existed inγ-Al2O3 phase even after calcinations.The results indicate that polyaluminum chloride with high Al13 content is an effective material to prepareγ-Al2O3.展开更多
A polyaluminium chloride solution with high Al 13 content self-prepared was used as material for preparing the spherical γ-Al 2 O 3 by the sol-gel and oil-drop method. Polyethylene glycol with different molecular mas...A polyaluminium chloride solution with high Al 13 content self-prepared was used as material for preparing the spherical γ-Al 2 O 3 by the sol-gel and oil-drop method. Polyethylene glycol with different molecular mass was used as surfactant to investigate the effect on property of γ-Al 2 O 3 . The physical property was characterized by 27 Al NMR (nuclear magnetic resonance) spectra, X-ray diffraction, FT-IR (Fourier transform infrared spectroscopy) and TG-DTA (thermogravimetric-differential thermal analysis). The results showed that surface area, pore volume and pore size of γ-Al 2 O 3 all increased with the increase of polyethylene glycol molecular mass in the experimental research range, and polyethylene glycol 10000 was the most suitable pore forming additive. γ-Al 2 O 3 with surface area of 339 m 2 ·g 1 , pore volume of 0.59 cm 3 ·g 1 and pore diameter of 6.9 nm were obtained at 450 °C.展开更多
基金Supported by National Natural Science Foundation of China（50708109 40673003） the Scientific Research Foundation for the Returned Overseas Chinese Scholars State Education Ministry（ITLXHG2009071702） the Special Fund from the State Key Laboratory of Environmental Aquatic Chemistry（09Y02ESPCR）
文摘In this paper a polyaluminum chloride solution with high Al13 content was prepared and used as raw material for preparation ofγ-Al2O3.The texture and crystalline phase of the prepared alumina samples were characterized by energy dispersive X-ray spectroscopy(EDX) ,X-ray diffraction,transmission electron microscope(TEM) and nuclear magnetic resonance(NMR) analyses.The effects of alkaline solution and calcination temperature were investigated.The results showed that alkaline solution including NH3·H2O and NaOH had little effect on the alumina sample formation.The impurities of NH4Cl and NaCl in solution can be removed through repeated washing by EDX analysis.Calcination temperature had a significant effect on alumina crystal phase.The alumina sample can transform completely toγ-Al2O3 in the subsequent heating from 600°C to 800°C.It is very interesting that Al13 can be existed inγ-Al2O3 phase even after calcinations.The results indicate that polyaluminum chloride with high Al13 content is an effective material to prepareγ-Al2O3.
基金Supported by the National Natural Science Foundation of China (21076219)the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministry (ITLXHG2009071702)
文摘A polyaluminium chloride solution with high Al 13 content self-prepared was used as material for preparing the spherical γ-Al 2 O 3 by the sol-gel and oil-drop method. Polyethylene glycol with different molecular mass was used as surfactant to investigate the effect on property of γ-Al 2 O 3 . The physical property was characterized by 27 Al NMR (nuclear magnetic resonance) spectra, X-ray diffraction, FT-IR (Fourier transform infrared spectroscopy) and TG-DTA (thermogravimetric-differential thermal analysis). The results showed that surface area, pore volume and pore size of γ-Al 2 O 3 all increased with the increase of polyethylene glycol molecular mass in the experimental research range, and polyethylene glycol 10000 was the most suitable pore forming additive. γ-Al 2 O 3 with surface area of 339 m 2 ·g 1 , pore volume of 0.59 cm 3 ·g 1 and pore diameter of 6.9 nm were obtained at 450 °C.