ZSM-5 zeolite membrane reactor was used in ethylbenzene dehydrogenation to styrene under the circumstances of commercial production.The experimental results indicated that the conversion of ethylbenzene in the membran...ZSM-5 zeolite membrane reactor was used in ethylbenzene dehydrogenation to styrene under the circumstances of commercial production.The experimental results indicated that the conversion of ethylbenzene in the membrane reactor increased with increasing pressure of the membrane tube.Using the inert sweep gas instead of vacuumizing, the result of long term steady operation under the same condition showed that the selectivity of styrene increased and the conversion of ethylbenzene in the membrane reactor increased by 7.52% in comparison with the fixed-bed reactor.展开更多
High-permeance ZSM-5 zeolite membrane was prepared on porous tubular α-Al 2O 3 support by varying-temperature hydrothermal synthesis. XRD patterns show that the membrane consists of ZSM-5 zeolite crystals. SEM analys...High-permeance ZSM-5 zeolite membrane was prepared on porous tubular α-Al 2O 3 support by varying-temperature hydrothermal synthesis. XRD patterns show that the membrane consists of ZSM-5 zeolite crystals. SEM analysis indicates that few defects exist in the membrane and the thickness of the membrane is about 9 μm. The hydrogen permeance through the membrane is about 2.4×10 -6 mol/(m 2·s·Pa), and the separation factor for n-C 4H 10/i-C 4H 10 mixture (volume ratio 1∶1) is 40, which indicates that it has a high quality with high permeance and selectivity. Repeated nucleation and re-growth of the crystals on the support result in the dense membrane formation.展开更多
文摘ZSM-5 zeolite membrane reactor was used in ethylbenzene dehydrogenation to styrene under the circumstances of commercial production.The experimental results indicated that the conversion of ethylbenzene in the membrane reactor increased with increasing pressure of the membrane tube.Using the inert sweep gas instead of vacuumizing, the result of long term steady operation under the same condition showed that the selectivity of styrene increased and the conversion of ethylbenzene in the membrane reactor increased by 7.52% in comparison with the fixed-bed reactor.
文摘High-permeance ZSM-5 zeolite membrane was prepared on porous tubular α-Al 2O 3 support by varying-temperature hydrothermal synthesis. XRD patterns show that the membrane consists of ZSM-5 zeolite crystals. SEM analysis indicates that few defects exist in the membrane and the thickness of the membrane is about 9 μm. The hydrogen permeance through the membrane is about 2.4×10 -6 mol/(m 2·s·Pa), and the separation factor for n-C 4H 10/i-C 4H 10 mixture (volume ratio 1∶1) is 40, which indicates that it has a high quality with high permeance and selectivity. Repeated nucleation and re-growth of the crystals on the support result in the dense membrane formation.