The reason why elongation of copper bars with columnar grains drops significantly after small cold-drawing was explored. The copper bars were prepared by warm-mould continuous casting. Tensile test was interrupted at ...The reason why elongation of copper bars with columnar grains drops significantly after small cold-drawing was explored. The copper bars were prepared by warm-mould continuous casting. Tensile test was interrupted at various tensile strains in order to detect crack origin. Electron backscattered diffraction（EBSD） was used to analyze dislocation slip bands. It is found that the as-cast microstructure contains sharp grain boundary（GB） corners nearly parallel to the solidification direction（SD）. Elongation of the copper bars drops significantly from 68.8% in as-cast state to 18.8% in as-drawn state. It is revealed that plastic deformation becomes severer in the vicinity of sharp GB corners. Locally accumulated internal stress even activates a slip system with very low Schmid factor of 0.17. The localized plastic deformation near sharp grain boundary corner promotes crack initiation and propagation, which eventually leads to the significant drop of elongation.展开更多
基金Project(2016YFB0301300) supported by the National Key R&D Program of ChinaProject(51674027) supported by the National Natural Science Foundation of China+1 种基金Project(2152020) supported by Beijing Natural Science Foundation,ChinaProject(2015AA034304) supported by the National High-Tech Research and Development Program of China
文摘The reason why elongation of copper bars with columnar grains drops significantly after small cold-drawing was explored. The copper bars were prepared by warm-mould continuous casting. Tensile test was interrupted at various tensile strains in order to detect crack origin. Electron backscattered diffraction（EBSD） was used to analyze dislocation slip bands. It is found that the as-cast microstructure contains sharp grain boundary（GB） corners nearly parallel to the solidification direction（SD）. Elongation of the copper bars drops significantly from 68.8% in as-cast state to 18.8% in as-drawn state. It is revealed that plastic deformation becomes severer in the vicinity of sharp GB corners. Locally accumulated internal stress even activates a slip system with very low Schmid factor of 0.17. The localized plastic deformation near sharp grain boundary corner promotes crack initiation and propagation, which eventually leads to the significant drop of elongation.