Effects of aging time and alkalinity as well as cation concentration(Na+) on the synthesis of A type zeolite and zeolite membrane were investigated in this paper. The results showed that aging time for synthesis of A ...Effects of aging time and alkalinity as well as cation concentration(Na+) on the synthesis of A type zeolite and zeolite membrane were investigated in this paper. The results showed that aging time for synthesis of A type zeolite and zeolite membrane had remarkable influence and alkalinity could accelerate the formation of zeolite but was disadvantage to zeolite membrane synthesis. Cation concentration(Na+) also couldn′t accelerate the synthesis of zeolite and zeolite membrane but it was probable an important factor to accelerate crystal growth .Moreover, more compact zeolite membranes could be synthesized by this method while the thickness of membrane was thinner than that of convention. Zeolites and zeolite membranes were characterized by XRD, TEM as well as IR characterization techniques.展开更多
Effect of different alkali metal salts on the crystal size and the crystallization rate of ZSM 5 zeolite was detailedly investigated in this paper. The samples prepared by adding the different alkali metal salts were ...Effect of different alkali metal salts on the crystal size and the crystallization rate of ZSM 5 zeolite was detailedly investigated in this paper. The samples prepared by adding the different alkali metal salts were characterized by using XRD, TEM, TG DSC, BET and IR techniques. The XRD results showed that, for the nanosized ZSM 5 zeolite, the characteristic peaks broadened on the XRD patterns in comparison with the microsized ZSM 5 zeolite. The SEM results verified that the crystal size of zeolites prepared by adding different alkali metal salts had different results, and adding NaCl, NaC2H3O2 and KCl showed the better effect of reducing crystal size, which are about of 40～ 60nm size. The crystallization curve of adding the different alkali metal salts suggested that the crystallization rate was significantly affected by the anions in the alkali metal salt besides the cations. Moreover, the crystal size likewise depended on the anion in the alkali metal salt. In addition, the BET results suggested that the nanosized ZSM 5 zeolite possessed a larger outer surface area in comparison with the microsized ZSM 5 zeolite. The thermostability of the samples was determined by TG DSC technique, indicating that the nanosized ZSM 5 zeolite had a poor thermostability as compared with the microsized ZSM 5 zeolite. The possible difference of the samples with different crystal sizes on IR spectra was also given.展开更多
文摘Effects of aging time and alkalinity as well as cation concentration(Na+) on the synthesis of A type zeolite and zeolite membrane were investigated in this paper. The results showed that aging time for synthesis of A type zeolite and zeolite membrane had remarkable influence and alkalinity could accelerate the formation of zeolite but was disadvantage to zeolite membrane synthesis. Cation concentration(Na+) also couldn′t accelerate the synthesis of zeolite and zeolite membrane but it was probable an important factor to accelerate crystal growth .Moreover, more compact zeolite membranes could be synthesized by this method while the thickness of membrane was thinner than that of convention. Zeolites and zeolite membranes were characterized by XRD, TEM as well as IR characterization techniques.
文摘Effect of different alkali metal salts on the crystal size and the crystallization rate of ZSM 5 zeolite was detailedly investigated in this paper. The samples prepared by adding the different alkali metal salts were characterized by using XRD, TEM, TG DSC, BET and IR techniques. The XRD results showed that, for the nanosized ZSM 5 zeolite, the characteristic peaks broadened on the XRD patterns in comparison with the microsized ZSM 5 zeolite. The SEM results verified that the crystal size of zeolites prepared by adding different alkali metal salts had different results, and adding NaCl, NaC2H3O2 and KCl showed the better effect of reducing crystal size, which are about of 40～ 60nm size. The crystallization curve of adding the different alkali metal salts suggested that the crystallization rate was significantly affected by the anions in the alkali metal salt besides the cations. Moreover, the crystal size likewise depended on the anion in the alkali metal salt. In addition, the BET results suggested that the nanosized ZSM 5 zeolite possessed a larger outer surface area in comparison with the microsized ZSM 5 zeolite. The thermostability of the samples was determined by TG DSC technique, indicating that the nanosized ZSM 5 zeolite had a poor thermostability as compared with the microsized ZSM 5 zeolite. The possible difference of the samples with different crystal sizes on IR spectra was also given.