In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches ...In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches a maximum value when the concentration of Tm3＋ is about 1.28 mol%, then it decreases rapidly as the concentration of Tm3＋ further increases to 3.49 mol%. The emission lifetime at 1.8 p.m also shows a similar tendency to the emission intensity. The maximum lifetime of 1.8 μm is measured to be 17.68 ms for the sample doped with Tm3＋ of 1.28 mol%. The emission cross section of 3F4 level is calculated. The maximum reaches 3.76 × 10 -21 cm2 at 1909 nm. The cross relaxation （3H6, 3H4 →3 F4, 3F4） between Tm3＋ ions and the concentration quenching effect are mainly attributed to the change of emission with Tm3＋ concentration. The largest quantum efficiency between Tm3＋ ions is estimated to be ,-147% from the measured lifetime and calculated radiative lifetime. All the results suggest that the Tm3＋/LiYF4 single crystal may have potential applications in 2 μm mid-infrared lasers.展开更多
Lithium lutetium fluoride(LiLuF4) single crystals doped with different Dy3+ ion concentrations were grown by Bridgman method. The Judd-Ofelt(J-O) strength parameters(Ω2, Ω4, Ω6) of Dy3+ in LiLuF4 crystal are calcul...Lithium lutetium fluoride(LiLuF4) single crystals doped with different Dy3+ ion concentrations were grown by Bridgman method. The Judd-Ofelt(J-O) strength parameters(Ω2, Ω4, Ω6) of Dy3+ in LiLuF4 crystal are calculated according to the measured absorption spectra and the J-O theory, by which the asymmetry of the Dy3+:LiLuF4 single crystal and the possibility of attaining stimulated emission from 4F9/2 level are analyzed. The capability of the Dy3+:LiLuF4 crystal in generating white light by simultaneous blue and yellow emissions under excitation with ultraviolet light is produced. The effects of excitation wavelength and doping concentration on chromaticity coordinates and photoluminescence intensity are also investigated. Favorable CIE coordinates, x=0.319 3 and y=0.349 3, can be obtained for Dy3+ ion in 2.701% molar doping concentration under excitation of 350 nm.展开更多
Ho3+ with various concentrations and Tm3+ with molar concentration of 1.28% are co-doped in Li YF4(YLF) single crystals. The luminescent properties of the crystals are investigated through emission spectra, emission c...Ho3+ with various concentrations and Tm3+ with molar concentration of 1.28% are co-doped in Li YF4(YLF) single crystals. The luminescent properties of the crystals are investigated through emission spectra, emission cross section and decay curves under the excitation of 808 nm. The energy transfer from Tm3+ to Ho3+ and the optimum fluorescence emission of Ho3+ around 2.05 μm are investigated. The emission intensity at 2.05 μm keeps increasing with the molar concentration of Ho3+ improved from 0.50% to 1.51% when the molar concentration of Tm3+ is kept at 1.28%. Moreover, for the co-doped crystals in which the molar concentrations of Tm3+ and Ho3+ are 1.28% and 1.51%, respectively, the maximum emission cross section reaches 0.760×10–20 cm2 and the maximum fluorescence lifetime is 21.98 ms. All the parameters suggest that these materials have more advantages in the future 2.0 μm laser applications.展开更多
基金supported by the National Natural Science Foundation of China(51272109)Natural Science Foundation of Ningbo City,China(201401A6105016,2013A610126)K.C.Wong Magna Fund in Ningbo University,China(NBUWC001)~~
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51472125 and 51272109)the Natural Science Foundation of Ningbo City,China(Grant No.201401A6105016)K.C.Wong Magna Fund in Ningbo University,China(Grant No.NBUWC001)
文摘In this paper, optical spectra of LiYF4 single crystals doped with Tm3＋ ions of various concentrations are reported. The emission intensity at 1.8 ktm first increases with increasing Tm3＋ concentration, and reaches a maximum value when the concentration of Tm3＋ is about 1.28 mol%, then it decreases rapidly as the concentration of Tm3＋ further increases to 3.49 mol%. The emission lifetime at 1.8 p.m also shows a similar tendency to the emission intensity. The maximum lifetime of 1.8 μm is measured to be 17.68 ms for the sample doped with Tm3＋ of 1.28 mol%. The emission cross section of 3F4 level is calculated. The maximum reaches 3.76 × 10 -21 cm2 at 1909 nm. The cross relaxation （3H6, 3H4 →3 F4, 3F4） between Tm3＋ ions and the concentration quenching effect are mainly attributed to the change of emission with Tm3＋ concentration. The largest quantum efficiency between Tm3＋ ions is estimated to be ,-147% from the measured lifetime and calculated radiative lifetime. All the results suggest that the Tm3＋/LiYF4 single crystal may have potential applications in 2 μm mid-infrared lasers.
基金supported by the National Natural Science Foundation of China(Nos.51272109 and 11374044)the Natural Science Foundation of Ningbo city(No.201401A6105016)K.C.Wong Magna Fund in Ningbo University
文摘Lithium lutetium fluoride(LiLuF4) single crystals doped with different Dy3+ ion concentrations were grown by Bridgman method. The Judd-Ofelt(J-O) strength parameters(Ω2, Ω4, Ω6) of Dy3+ in LiLuF4 crystal are calculated according to the measured absorption spectra and the J-O theory, by which the asymmetry of the Dy3+:LiLuF4 single crystal and the possibility of attaining stimulated emission from 4F9/2 level are analyzed. The capability of the Dy3+:LiLuF4 crystal in generating white light by simultaneous blue and yellow emissions under excitation with ultraviolet light is produced. The effects of excitation wavelength and doping concentration on chromaticity coordinates and photoluminescence intensity are also investigated. Favorable CIE coordinates, x=0.319 3 and y=0.349 3, can be obtained for Dy3+ ion in 2.701% molar doping concentration under excitation of 350 nm.
基金supported by the National Natural Science Foundation of China(Nos.51472125 and 51272109)the Natural Science Foundation of Ningbo City(No.201401A6105016)K.C.Wong Magna Fund in Ningbo University
文摘Ho3+ with various concentrations and Tm3+ with molar concentration of 1.28% are co-doped in Li YF4(YLF) single crystals. The luminescent properties of the crystals are investigated through emission spectra, emission cross section and decay curves under the excitation of 808 nm. The energy transfer from Tm3+ to Ho3+ and the optimum fluorescence emission of Ho3+ around 2.05 μm are investigated. The emission intensity at 2.05 μm keeps increasing with the molar concentration of Ho3+ improved from 0.50% to 1.51% when the molar concentration of Tm3+ is kept at 1.28%. Moreover, for the co-doped crystals in which the molar concentrations of Tm3+ and Ho3+ are 1.28% and 1.51%, respectively, the maximum emission cross section reaches 0.760×10–20 cm2 and the maximum fluorescence lifetime is 21.98 ms. All the parameters suggest that these materials have more advantages in the future 2.0 μm laser applications.