Burnt lime and serpentine were incorporated into the sinter mix to improve high iron and low silica sinte-ring. Optimization of how to use burnt lime including dosage of burnt lime, moisture of sinter mix, hydrating a...Burnt lime and serpentine were incorporated into the sinter mix to improve high iron and low silica sinte-ring. Optimization of how to use burnt lime including dosage of burnt lime, moisture of sinter mix, hydrating andgranulation time was performed. Evaluations of sinter characteristics including sinter mineralogy, reducibility, lowtemperature reduction degradation, softening and melting down properties were carried out. Compared with the re-sults of traditional process in base case, the tumbling index (TI) is increased by 1.53%-2.33% through proportio-ning high ratio of burnt lime or adding serpentine in the sinter mix. It is shown that effective granulation, better per-meability and improved high temperature reactivity in the sinter bed are achieved, resulting in an increase in 3.13 %- 5.10% calcium ferrite occurring in acicular and columnar shape and decrease in glass phase, and with the reduc-ibility index(RI) being increased by 1.65%- 3.25%.展开更多
基金Project(2000-26) supported by the Foundation for the Teaching and Research Program for Outstanding Young Teachers in Higher Education Institutions of Education Ministry, China
文摘Burnt lime and serpentine were incorporated into the sinter mix to improve high iron and low silica sinte-ring. Optimization of how to use burnt lime including dosage of burnt lime, moisture of sinter mix, hydrating andgranulation time was performed. Evaluations of sinter characteristics including sinter mineralogy, reducibility, lowtemperature reduction degradation, softening and melting down properties were carried out. Compared with the re-sults of traditional process in base case, the tumbling index (TI) is increased by 1.53%-2.33% through proportio-ning high ratio of burnt lime or adding serpentine in the sinter mix. It is shown that effective granulation, better per-meability and improved high temperature reactivity in the sinter bed are achieved, resulting in an increase in 3.13 %- 5.10% calcium ferrite occurring in acicular and columnar shape and decrease in glass phase, and with the reduc-ibility index(RI) being increased by 1.65%- 3.25%.