We investigate the influence of precursor molar ratio of [S^2-]/[Zn^2＋] on particle size and photoluminescence （PL） of ZnS：Mn^2＋ nanocrystMs. By changing the [S^2-]/[Zn^2＋] ratio from 0.6 （Zn-rich） to 2.0 （S-...We investigate the influence of precursor molar ratio of [S^2-]/[Zn^2＋] on particle size and photoluminescence （PL） of ZnS：Mn^2＋ nanocrystMs. By changing the [S^2-]/[Zn^2＋] ratio from 0.6 （Zn-rich） to 2.0 （S-rich）, the particle size increases from nearly 2. 7nm to about 4.Ohm. The increase in the ratio of [S^2-]/[Zn^2＋] cadses a decrease of PL emission intensity of ZnS host while a distinct increase of Mn^2＋ emission. The maximum intensity for the luminescence of Mn^2＋ emission is observed at the ratio of [S^2-]/[Zn^2＋] ≈ 1.5. The possible mechanism for the results is discussed by filling of S^2- vacancies and the increase of Mn^2＋ ions incorporated into ZnS lattices.展开更多
Spherical organic-bonded ZnS nanocrystals with 4.0 4-0.2 nm in diameter are synthesized by a liquid-solid-solution method. The photoluminescence spectrum of sample （[S^2-]/[Zn^2＋] = 1.0） shows a strong white emissi...Spherical organic-bonded ZnS nanocrystals with 4.0 4-0.2 nm in diameter are synthesized by a liquid-solid-solution method. The photoluminescence spectrum of sample （[S^2-]/[Zn^2＋] = 1.0） shows a strong white emission with a peak at 490nm and - 170 nm full widths at half maximum. By Gauss fitting, the white emission is attributed to the overlap of a blue emission and a green-yellow emission, originating from electronic transitions from internal S^2- vacancies level to valence band and to the internal Zn^2＋ vacancy level, respectively. After sealingZnS nanocrystals onto InGaN chips, the device shows CIE coordinates of （0.29,0.30）, which indicates their potential applications for white light emitting diodes.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 10674074, and the Tianjin Natural Science Foundation under Grant Nos 06TXTJJC14601 and 07JCYBJC06400.
文摘We investigate the influence of precursor molar ratio of [S^2-]/[Zn^2＋] on particle size and photoluminescence （PL） of ZnS：Mn^2＋ nanocrystMs. By changing the [S^2-]/[Zn^2＋] ratio from 0.6 （Zn-rich） to 2.0 （S-rich）, the particle size increases from nearly 2. 7nm to about 4.Ohm. The increase in the ratio of [S^2-]/[Zn^2＋] cadses a decrease of PL emission intensity of ZnS host while a distinct increase of Mn^2＋ emission. The maximum intensity for the luminescence of Mn^2＋ emission is observed at the ratio of [S^2-]/[Zn^2＋] ≈ 1.5. The possible mechanism for the results is discussed by filling of S^2- vacancies and the increase of Mn^2＋ ions incorporated into ZnS lattices.
基金Supported by the National Natural Science Foundation of China under Grant Nos 60877029, 60977035, 60907021 and 10904109, and the Natural Science Foundation of Tianjin under Grant Nos 09JCYBJC01400, 07JCYBJC06400 and the Natural Science Foundation of Tianjin Education Committee under Grant No 20071207.
文摘Spherical organic-bonded ZnS nanocrystals with 4.0 4-0.2 nm in diameter are synthesized by a liquid-solid-solution method. The photoluminescence spectrum of sample （[S^2-]/[Zn^2＋] = 1.0） shows a strong white emission with a peak at 490nm and - 170 nm full widths at half maximum. By Gauss fitting, the white emission is attributed to the overlap of a blue emission and a green-yellow emission, originating from electronic transitions from internal S^2- vacancies level to valence band and to the internal Zn^2＋ vacancy level, respectively. After sealingZnS nanocrystals onto InGaN chips, the device shows CIE coordinates of （0.29,0.30）, which indicates their potential applications for white light emitting diodes.