Effects of initial δ phase（Ni_3Nb） on the hot tensile deformation behaviors and material constants of a Ni-based superalloy were investigated over wide ranges of strain rate and deformation temperature. It is found...Effects of initial δ phase（Ni_3Nb） on the hot tensile deformation behaviors and material constants of a Ni-based superalloy were investigated over wide ranges of strain rate and deformation temperature. It is found that the true stress-true strain curves exhibit peak stress at a small strain, and the peak stress increases with the increase of initial δ phase. After the peak stress, initial δ phase promotes the dynamic softening behaviors, resulting in the decreased flow stress. An improved Arrhenius constitutive model is proposed to consider the synthetical effects of initial δ phase, deformation temperature, strain rate, and strain on hot deformation behaviors. In the improved model, material constants are expressed as the functions of the content of initial δ phase and strain. A good agreement between the predicted and measured results indicates that the improved Arrhenius constitutive model can well describe hot deformation behaviors of the studied Ni-based superalloy.展开更多
基金Projects(5137550251305466) supported by the National Natural Science Foundation of China+2 种基金Project(2015CX002) supported by the Innovation-driven Plan in Central South University,ChinaProject(2013CB035801) supported by the National Basic Research Program of ChinaProject(2015NGQ001) supported by Key Laboratory of Efficient&Clean Energy Utilization,College of Hunan Province,China
文摘Effects of initial δ phase（Ni_3Nb） on the hot tensile deformation behaviors and material constants of a Ni-based superalloy were investigated over wide ranges of strain rate and deformation temperature. It is found that the true stress-true strain curves exhibit peak stress at a small strain, and the peak stress increases with the increase of initial δ phase. After the peak stress, initial δ phase promotes the dynamic softening behaviors, resulting in the decreased flow stress. An improved Arrhenius constitutive model is proposed to consider the synthetical effects of initial δ phase, deformation temperature, strain rate, and strain on hot deformation behaviors. In the improved model, material constants are expressed as the functions of the content of initial δ phase and strain. A good agreement between the predicted and measured results indicates that the improved Arrhenius constitutive model can well describe hot deformation behaviors of the studied Ni-based superalloy.