云南某低品位黏土型锂矿石含锂0.147%,为探究低能耗、环保的开发利用工艺,采用新型焙烧助剂ASH开展了低温焙烧—无酸浸出的提锂工艺研究,并结合XRD、SEM-EDS等分析手段阐述了反应机理。试验结果表明,在试样与ASH质量比为1∶0.3、焙烧温...云南某低品位黏土型锂矿石含锂0.147%,为探究低能耗、环保的开发利用工艺,采用新型焙烧助剂ASH开展了低温焙烧—无酸浸出的提锂工艺研究,并结合XRD、SEM-EDS等分析手段阐述了反应机理。试验结果表明,在试样与ASH质量比为1∶0.3、焙烧温度为400℃、焙烧时间为1.0 h,去离子水浸出时间为2 h、浸出温度为70℃、液固比为5 m L/g条件下,锂浸出率为83.81%。机理分析显示,焙烧—浸出前后,样品中主要矿物相未发生变化,但衍射峰强度降低;经焙烧—浸出后,浸渣表面均匀分布着裂纹和空隙,Al、Si、Fe、Ti含量均有所降低。说明ASH与矿物发生反应,破坏了矿物的表面结构,生成了可溶性盐Li-ASH。与传统焙烧—浸出工艺相比,本研究所采用的提锂工艺焙烧温度低、浸出时无酸,降低了生产能耗、简化了工艺流程,对同类型低品位黏土型锂矿的绿色高效开发利用具有重要借鉴意义。展开更多
The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geop...The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geopolymers with compressive strength of 38.8 MPa were prepared by using phosphate tailings as the main raw material,fly ash as the active silicon-aluminum material,and water glass as the alkaline activator.The solid content of phosphate tailings and fly ash was 60% and 40%,respectively,and the water-cement ratio was 0.22.The results of XRD,FTIR,SEM-EDS and XPS show that the reactivity of phosphate tailings with alkaline activator is weak,and the silicon-aluminum material can react with alkaline activator to form zeolite and gel,and encapsulate/cover the phosphate tailings to form a dense phosphate tailings-based geopolymer.During the formation of geopolymers,part of the aluminum-oxygen tetrahedron replaced the silicon-oxygen tetrahedron,causing the polycondensation reaction between geopolymers and increasing the strength of geopolymers.The leaching toxicity test results show that the geopolymer has a good solid sealing effect on heavy metal ions.The preparation of geopolymer from phosphate tailings is an important way to alleviate the storage pressure and realize the resource utilization of phosphate tailings.展开更多
文摘云南某低品位黏土型锂矿石含锂0.147%,为探究低能耗、环保的开发利用工艺,采用新型焙烧助剂ASH开展了低温焙烧—无酸浸出的提锂工艺研究,并结合XRD、SEM-EDS等分析手段阐述了反应机理。试验结果表明,在试样与ASH质量比为1∶0.3、焙烧温度为400℃、焙烧时间为1.0 h,去离子水浸出时间为2 h、浸出温度为70℃、液固比为5 m L/g条件下,锂浸出率为83.81%。机理分析显示,焙烧—浸出前后,样品中主要矿物相未发生变化,但衍射峰强度降低;经焙烧—浸出后,浸渣表面均匀分布着裂纹和空隙,Al、Si、Fe、Ti含量均有所降低。说明ASH与矿物发生反应,破坏了矿物的表面结构,生成了可溶性盐Li-ASH。与传统焙烧—浸出工艺相比,本研究所采用的提锂工艺焙烧温度低、浸出时无酸,降低了生产能耗、简化了工艺流程,对同类型低品位黏土型锂矿的绿色高效开发利用具有重要借鉴意义。
基金Project(202202AG050010)supported by the Yunnan Major Scientific and Technological Projects,ChinaProject(202103AA080007)supported by the Key R&D Project of Science and Technology Department of Yunnan Province,ChinaProject(NECP2023-06)supported by the Open Project Fund of National Engineering and Technology Research Center for Development&Utilization of Phosphorous Resources,China。
文摘The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geopolymers with compressive strength of 38.8 MPa were prepared by using phosphate tailings as the main raw material,fly ash as the active silicon-aluminum material,and water glass as the alkaline activator.The solid content of phosphate tailings and fly ash was 60% and 40%,respectively,and the water-cement ratio was 0.22.The results of XRD,FTIR,SEM-EDS and XPS show that the reactivity of phosphate tailings with alkaline activator is weak,and the silicon-aluminum material can react with alkaline activator to form zeolite and gel,and encapsulate/cover the phosphate tailings to form a dense phosphate tailings-based geopolymer.During the formation of geopolymers,part of the aluminum-oxygen tetrahedron replaced the silicon-oxygen tetrahedron,causing the polycondensation reaction between geopolymers and increasing the strength of geopolymers.The leaching toxicity test results show that the geopolymer has a good solid sealing effect on heavy metal ions.The preparation of geopolymer from phosphate tailings is an important way to alleviate the storage pressure and realize the resource utilization of phosphate tailings.