Besides Li＋ and Mg2＋, the electrochemical behavior of Na^＋ and K＋ in LiFePO4/FePO4 structures was studied since they naturally coexist with Li＋ and Mg2＋ in brine. The cyclic voltammogram （CV） results indicated...Besides Li＋ and Mg2＋, the electrochemical behavior of Na^＋ and K＋ in LiFePO4/FePO4 structures was studied since they naturally coexist with Li＋ and Mg2＋ in brine. The cyclic voltammogram （CV） results indicated that Na＋ exhibits some reversibility in LiFePO4/FePO4 structures. Its reduction peak appears at -0.511 V, more negative than that of Li＋ （-0.197 V）, meaning that a relatively positive potential is beneficial for decreasing Na＋ insertion. The reduction peak of K＋ could not be found clearly, indicating that K＋ is difficult to insert into the FePO4 structure. Furthermore, technical experiments using real brine with a super high Mg/Li ratio （493） at a cell voltage of 0.7V showed that the final extracted capacity of Li＋, Mg2＋ and Na＋ that can be attained in 1 g LiFePO4 is 24.1 mg, 7.32 mg and 4.61 mg, respectively. The Mg/Li ratio can be reduced to 0.30 from 493, and the Na/Li ratio to 0.19 from 16.7, which proves that, even in super high Mg/Li ratio brine, if a cell voltage is appropriately controlled, it is possible to separate Li^＋ and other impurities effectively.展开更多
The adsorption behavior of D301 for molybdenum blue was investigated.The thermodynamics parameters in adsorption process were calculated and the adsorption kinetics was studied.The experimental results show that the a...The adsorption behavior of D301 for molybdenum blue was investigated.The thermodynamics parameters in adsorption process were calculated and the adsorption kinetics was studied.The experimental results show that the adsorption characteristic of D301 for molybdenum blue fits well with the Freundlich adsorption isotherm equation.In the adsorption process of D301 for molybdenum blue,both the enthalpy change ΔH and entropy change ΔS are positive,while the free energy change ΔG is negative when temperatures are in the range of 303-333 K.It is indicated that the adsorption is a spontaneous and endothermic process,and the elevated temperatures benefit to the adsorption.Kinetic studies show that the kinetic data are well described by double driving-force model,and the adsorption rate of molybdenum blue on D301 is controlled by the intraparticle diffusion during the adsorption process.The total kinetic equation is determined.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 52174340, 51704338)the Basic Science Center of the National Natural Science Foundation of China (No. 72088101)the National Key Research and Development Project of China (No. 2022YFC2904505)。
基金Project(K1205034-11) supported by Technology Program of Changsha,China
文摘Besides Li＋ and Mg2＋, the electrochemical behavior of Na^＋ and K＋ in LiFePO4/FePO4 structures was studied since they naturally coexist with Li＋ and Mg2＋ in brine. The cyclic voltammogram （CV） results indicated that Na＋ exhibits some reversibility in LiFePO4/FePO4 structures. Its reduction peak appears at -0.511 V, more negative than that of Li＋ （-0.197 V）, meaning that a relatively positive potential is beneficial for decreasing Na＋ insertion. The reduction peak of K＋ could not be found clearly, indicating that K＋ is difficult to insert into the FePO4 structure. Furthermore, technical experiments using real brine with a super high Mg/Li ratio （493） at a cell voltage of 0.7V showed that the final extracted capacity of Li＋, Mg2＋ and Na＋ that can be attained in 1 g LiFePO4 is 24.1 mg, 7.32 mg and 4.61 mg, respectively. The Mg/Li ratio can be reduced to 0.30 from 493, and the Na/Li ratio to 0.19 from 16.7, which proves that, even in super high Mg/Li ratio brine, if a cell voltage is appropriately controlled, it is possible to separate Li^＋ and other impurities effectively.
基金Project(2007AA06Z129) supported by the High-tech Research and Development Program of China
文摘The adsorption behavior of D301 for molybdenum blue was investigated.The thermodynamics parameters in adsorption process were calculated and the adsorption kinetics was studied.The experimental results show that the adsorption characteristic of D301 for molybdenum blue fits well with the Freundlich adsorption isotherm equation.In the adsorption process of D301 for molybdenum blue,both the enthalpy change ΔH and entropy change ΔS are positive,while the free energy change ΔG is negative when temperatures are in the range of 303-333 K.It is indicated that the adsorption is a spontaneous and endothermic process,and the elevated temperatures benefit to the adsorption.Kinetic studies show that the kinetic data are well described by double driving-force model,and the adsorption rate of molybdenum blue on D301 is controlled by the intraparticle diffusion during the adsorption process.The total kinetic equation is determined.