Self-assembly reaction of 1,2,4,5-benzenetetracarboxylic acid(H4 btc) with CuCl2 in mixed N,N-dimethylformamide(DMF), methanol and aqueous solution at room temperature generated a 2D complex, [Cu(btc)0.5(DMF)...Self-assembly reaction of 1,2,4,5-benzenetetracarboxylic acid(H4 btc) with CuCl2 in mixed N,N-dimethylformamide(DMF), methanol and aqueous solution at room temperature generated a 2D complex, [Cu(btc)0.5(DMF)(H2 O)]n(1) which was further characterized by X-ray diffraction, IR spectrum, elemental analysis and TG-DTA experiments. The structure determination reveals that the fundamental unit of complex 1 contains one Cu(Ⅱ) ion, half a btc4–, one DMF molecule and one water molecule, forming a half paddlewheel-like building block [Cu2(btc)(DMF)2(H2 O)2] which is different from those previous Cu-btc(Ⅱ) polymers obtained either in water or other media without water. It crystallizes in monoclinic system, space group C2/c with a = 22.8209(14), b = 9.2244(6), c = 10.8876(7) ?, b = 117.5210(10)o, V = 2032.6(2) ?3, Z = 2, C8 H10 CuNO6, Mr = 279.71, Dc = 1.828 g/cm3, μ = 2.162 mm-1, F(000) = 1136, the final R = 0.0225 and wR = 0.0652 with I 〉 2s(I). Furthermore, the thermal stability of complex 1 is observed to be dependent on the polymeric structure nature. And the luminescent measurements show that complex 1 produces strong emission at room temperature.展开更多
基金supported by the National Natural Science Foundation of China(No.21531005)
文摘Self-assembly reaction of 1,2,4,5-benzenetetracarboxylic acid(H4 btc) with CuCl2 in mixed N,N-dimethylformamide(DMF), methanol and aqueous solution at room temperature generated a 2D complex, [Cu(btc)0.5(DMF)(H2 O)]n(1) which was further characterized by X-ray diffraction, IR spectrum, elemental analysis and TG-DTA experiments. The structure determination reveals that the fundamental unit of complex 1 contains one Cu(Ⅱ) ion, half a btc4–, one DMF molecule and one water molecule, forming a half paddlewheel-like building block [Cu2(btc)(DMF)2(H2 O)2] which is different from those previous Cu-btc(Ⅱ) polymers obtained either in water or other media without water. It crystallizes in monoclinic system, space group C2/c with a = 22.8209(14), b = 9.2244(6), c = 10.8876(7) ?, b = 117.5210(10)o, V = 2032.6(2) ?3, Z = 2, C8 H10 CuNO6, Mr = 279.71, Dc = 1.828 g/cm3, μ = 2.162 mm-1, F(000) = 1136, the final R = 0.0225 and wR = 0.0652 with I 〉 2s(I). Furthermore, the thermal stability of complex 1 is observed to be dependent on the polymeric structure nature. And the luminescent measurements show that complex 1 produces strong emission at room temperature.