Graphene under high temperature was prepared and loaded on Ni foam.Then,cobalt tetroxide precursor was grown on Ni foam in situ by the hydrothermal method.Finally,the sample was burned at high temperature to obtain Co...Graphene under high temperature was prepared and loaded on Ni foam.Then,cobalt tetroxide precursor was grown on Ni foam in situ by the hydrothermal method.Finally,the sample was burned at high temperature to obtain Co_(3)O_(4)+graphene@Ni.The hydrothermal method used in this paper is easy to operate,with low-risk factors and environmental protection.The prepared Co_(3)O_(4)+graphene@Ni electrode exhibits superior electrochemical performance than Co_(3)O_(4)@Ni electrode.At a current density of 1 A/g,the specific capacitance of the Co_(3)O_(4)+graphene@Ni electrode calculated by a charge-discharge test is 935 F/g,which is much larger than that of Co_(3)O_(4)@Ni electrode of 340 F/g.展开更多
基金Project(21502014)supported by the National Natural Science Foundation of ChinaProjects(20180550736,2019-ZD 0117)supported by the Natural Science Foundation of Liaoning Province,China+1 种基金Projects(JDL 2019004,JDL 2017027)supported by the Research Foundation of Educational Committee of Liaoning Province,ChinaProject(191008-K)supported by Guangxi Key Laboratory of Information Materials(Guilin University of Electronic Technology),China。
文摘Graphene under high temperature was prepared and loaded on Ni foam.Then,cobalt tetroxide precursor was grown on Ni foam in situ by the hydrothermal method.Finally,the sample was burned at high temperature to obtain Co_(3)O_(4)+graphene@Ni.The hydrothermal method used in this paper is easy to operate,with low-risk factors and environmental protection.The prepared Co_(3)O_(4)+graphene@Ni electrode exhibits superior electrochemical performance than Co_(3)O_(4)@Ni electrode.At a current density of 1 A/g,the specific capacitance of the Co_(3)O_(4)+graphene@Ni electrode calculated by a charge-discharge test is 935 F/g,which is much larger than that of Co_(3)O_(4)@Ni electrode of 340 F/g.