A thermal-mechanical and micro-macro coupled finite element（FE） model for the hot extrusion process of large-scale thick-walled Inconel 625 pipe was developed based on the DEFORM-2D platform.Then,the influence rules...A thermal-mechanical and micro-macro coupled finite element（FE） model for the hot extrusion process of large-scale thick-walled Inconel 625 pipe was developed based on the DEFORM-2D platform.Then,the influence rules of the key extrusion parameters on the average grain size and grain uniformity of the extruded pipe were revealed.The results show that with the increase of initial billet temperature,extrusion speed and friction coefficient,the grain uniformity is firstly improved and then deteriorated.Larger extrusion ratio leads to more uniform grain distribution.With the increase of initial billet temperature,the average grain size of the pipe first decreases and then increases.Additionally,larger extrusion ratio can bring smaller average grain size.The extrusion speed and friction coefficient have slight effects on the average grain size of the extruded pipe.展开更多
基金Project(2009ZX04005-031-11)supported by the Major National Science and Technology Special Project of ChinaProject(KP200911)supported by the Research Fund of State Key Laboratory of Solidification Processing of ChinaProject(B08040)supported by the"111"Project of China
文摘A thermal-mechanical and micro-macro coupled finite element（FE） model for the hot extrusion process of large-scale thick-walled Inconel 625 pipe was developed based on the DEFORM-2D platform.Then,the influence rules of the key extrusion parameters on the average grain size and grain uniformity of the extruded pipe were revealed.The results show that with the increase of initial billet temperature,extrusion speed and friction coefficient,the grain uniformity is firstly improved and then deteriorated.Larger extrusion ratio leads to more uniform grain distribution.With the increase of initial billet temperature,the average grain size of the pipe first decreases and then increases.Additionally,larger extrusion ratio can bring smaller average grain size.The extrusion speed and friction coefficient have slight effects on the average grain size of the extruded pipe.
基金Project (2009ZX04005-031-11) supported by the National Major Science and Technology Special Program of ChinaProject ([2011]3008)supported by the State Foundation for Studying AbroadProject (B08040) supported by the 111 Project