Mn-doped ZnO nanocrystals are synthesized by a wet chemical route and treated in H2/Ar atmosphere with different H2/Ar ratios. It is found that hydrogen annealing could change the coordination environment of Mn in ZnO...Mn-doped ZnO nanocrystals are synthesized by a wet chemical route and treated in H2/Ar atmosphere with different H2/Ar ratios. It is found that hydrogen annealing could change the coordination environment of Mn in ZnO lattice and manipulate the magnetic properties of Mn-doped ZnO. Mn ions initially enter into interstitial sites and a Mn3＋ 06 octahedral coordination is produced in the prepared Mn-doped ZnO sample, in which the nearest neighbor Mn3＋ and 02 ions could form a Mn3＋-O2--Mn3＋ complex. After H2 annealing, interstitial Mn ions can substitute for Zn to generate the Mn2＋O4 tetrahedral coordination in the nanocrystals, in which neighboring Mn2＋ ions and H atoms could form a Mn2＋-O2--Mn2＋ complex and Mn-H-Mn bridge structure. The magnetic measurement of the as-prepared sample shows room temperature paramagnetic behavior due to the Mn3＋-O2--Mn3＋ complex, while the annealed samples exhibit their ferromagnetism, which originates from the Mn-H-Mn bridge structure and the Mn-Mn exchange interaction in the Mn2＋-O2--Mn2＋ complex.展开更多
基金supported by the National Basic Research Program of China(Grant No.2013CB934001)the National Natural Science Foundation of China(Grant Nos.51072012 and 51272015)
文摘Mn-doped ZnO nanocrystals are synthesized by a wet chemical route and treated in H2/Ar atmosphere with different H2/Ar ratios. It is found that hydrogen annealing could change the coordination environment of Mn in ZnO lattice and manipulate the magnetic properties of Mn-doped ZnO. Mn ions initially enter into interstitial sites and a Mn3＋ 06 octahedral coordination is produced in the prepared Mn-doped ZnO sample, in which the nearest neighbor Mn3＋ and 02 ions could form a Mn3＋-O2--Mn3＋ complex. After H2 annealing, interstitial Mn ions can substitute for Zn to generate the Mn2＋O4 tetrahedral coordination in the nanocrystals, in which neighboring Mn2＋ ions and H atoms could form a Mn2＋-O2--Mn2＋ complex and Mn-H-Mn bridge structure. The magnetic measurement of the as-prepared sample shows room temperature paramagnetic behavior due to the Mn3＋-O2--Mn3＋ complex, while the annealed samples exhibit their ferromagnetism, which originates from the Mn-H-Mn bridge structure and the Mn-Mn exchange interaction in the Mn2＋-O2--Mn2＋ complex.