在353K的乙酰胺-尿素-N aB r熔体中,P t、Cu电极上,Co(Ⅱ)+2e→Co(0)是一步完全不可逆反应,测得0.060m o l.L-1CoC l2-乙酰胺-尿素-N aB r中,Co(Ⅱ)在P t上,传递系数α=0.28,扩散系数D0=4.68×10-5cm2.-s 1,Cu上α=0.28,D0=4.06...在353K的乙酰胺-尿素-N aB r熔体中,P t、Cu电极上,Co(Ⅱ)+2e→Co(0)是一步完全不可逆反应,测得0.060m o l.L-1CoC l2-乙酰胺-尿素-N aB r中,Co(Ⅱ)在P t上,传递系数α=0.28,扩散系数D0=4.68×10-5cm2.-s 1,Cu上α=0.28,D0=4.06×1-0 7cm2.-s 1。G d(Ⅲ)不能单独还原为G d(0),但可以被Co(Ⅱ)诱导共沉积。由恒电位电解法得到非晶态的G d-Co合金,G d的含量随阴极电位的负移,G d(Ⅲ)/N i(Ⅱ)摩尔比增大以及电解时间延长而增大。展开更多
The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The...The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The uncrystallized alloy film of La-Ni is obtained by potentiostatic electrolysis, and the amount of La grows with increasing cathodic overpotential, molar ratios of La(Ⅲ) to Ni(Ⅱ) and the electrolysis time. The maximum amount of La in alloy film reaches to 78.81% (mass fraction) in present study.展开更多
The kinetics of La-Co alloy film in acetamide-urea-NaBr molten salt electrolyte at 353K was investigated. It is shown that the reduction of Co(Ⅱ) to Co is irreversible reaction with the transfer coefficient of 0.28...The kinetics of La-Co alloy film in acetamide-urea-NaBr molten salt electrolyte at 353K was investigated. It is shown that the reduction of Co(Ⅱ) to Co is irreversible reaction with the transfer coefficient of 0.28 and the diffusion coefficient of 7.46×10 -5 cm 2/s. While La(Ⅲ) cannot be reduced to La directly; but can be codeposited with cobalt. The content of La in the uncrystallized La-Co alloy film increases with increasing cathodic overpotential, molar ratio of La 3+ to Co 2+ and electrolysis time as well, and reaches the maximum of 66.32%.展开更多
文摘The reduction of Ni(Ⅱ) is an irreversible reaction and La(Ⅲ) cannot be reduced to La directly but be co-deposited inductively in the present of Ni(Ⅱ) in the Acetamide-Urea-NaBr molten salt electrolyte at 353 K. The uncrystallized alloy film of La-Ni is obtained by potentiostatic electrolysis, and the amount of La grows with increasing cathodic overpotential, molar ratios of La(Ⅲ) to Ni(Ⅱ) and the electrolysis time. The maximum amount of La in alloy film reaches to 78.81% (mass fraction) in present study.
文摘The kinetics of La-Co alloy film in acetamide-urea-NaBr molten salt electrolyte at 353K was investigated. It is shown that the reduction of Co(Ⅱ) to Co is irreversible reaction with the transfer coefficient of 0.28 and the diffusion coefficient of 7.46×10 -5 cm 2/s. While La(Ⅲ) cannot be reduced to La directly; but can be codeposited with cobalt. The content of La in the uncrystallized La-Co alloy film increases with increasing cathodic overpotential, molar ratio of La 3+ to Co 2+ and electrolysis time as well, and reaches the maximum of 66.32%.