Lead lanthanum zirconate stannate titanate （PLZST） powders with homogeneous composition were synthesized at a relatively low temperature of 650 ℃ by a citrate process based on the Pechini method. Clear aqueous solu...Lead lanthanum zirconate stannate titanate （PLZST） powders with homogeneous composition were synthesized at a relatively low temperature of 650 ℃ by a citrate process based on the Pechini method. Clear aqueous solutions were prepared from inorganic salts, and citric acid was added as a chelating agent to attain precursor sols. Dried gel-precursors were calcined at different temperatures for various time. The perovskites powders were obtained at 650 ℃ for 1 hour. XRD and SEM results show that the powders were single-phase and ultrafine particles.展开更多
基金the National Natural Science Foundation of China(No.50272030)
文摘Lead lanthanum zirconate stannate titanate （PLZST） powders with homogeneous composition were synthesized at a relatively low temperature of 650 ℃ by a citrate process based on the Pechini method. Clear aqueous solutions were prepared from inorganic salts, and citric acid was added as a chelating agent to attain precursor sols. Dried gel-precursors were calcined at different temperatures for various time. The perovskites powders were obtained at 650 ℃ for 1 hour. XRD and SEM results show that the powders were single-phase and ultrafine particles.