Conductive perovskite BaPb03 （BPO） films as a potential electrode material of PZT capacitors used in ferroelectric random access memory are prepared by rf magnetron sputtering. An x-ray diffractometer and standard f...Conductive perovskite BaPb03 （BPO） films as a potential electrode material of PZT capacitors used in ferroelectric random access memory are prepared by rf magnetron sputtering. An x-ray diffractometer and standard four probe method are employed to investigate the dependence of growth conditions on crystal structure and conductivity of BPO films. It is found that BPO films with perovskite phase can be obtained at substrate temperatures above 425℃, and the sample with the lowest resistivity is obtained at 450℃ under pure argon atmosphere. Using this BPO film as electrode, ferroelectric properties of BPO/PZT/BPO and Pt/PZT/BPO sandwiched structures are evaluated. Their remanent polarization and coercive field are 36.6 ℃/cm^2 （81.3 k V/cm） and 36.9℃/cm^2 （89.1 kV/cm）, respectively. The coercive field of the former structure is lower than that of the latter, but remanent polarizations are almost the same. In addition, the results imply that BPO electrode is helpful to improve the fatigue resistance of PZT. The reasons are discussed.展开更多
We investigate SrBi2 Ta2 O9 （SBT） films prepared by the sol-gel spin method with different spin rates or different anneal conditions for the first layer of SBT, as promising ferroelectric layer materials applied to ...We investigate SrBi2 Ta2 O9 （SBT） films prepared by the sol-gel spin method with different spin rates or different anneal conditions for the first layer of SBT, as promising ferroelectric layer materials applied to ferroelectric random access memory （FeRAM）. All the specimens in this experiment have similar SBT crystal orientations of （115）, （020）, （220）, and （135）. The Pt/SBT/Pt capacitor with coating of 3000rpm spin rate has a perfect rectangle shape of hysteresis loops, remanent polarization of 7.571μC/cm^2 and coercive voltage of 0.816 V at 5 V voltage amplitude. These characteristics are better than those with coating of 3500rpm spin rate, which is attributed to the influence for thickness and grain size of the film from depressed spin rate. Slow-rate anneal in the furnace for the first layer of SBT can improve the crystallization processes and properties for SBT layers slightly, compared with rapid thermal annealing. The ion damage from etching for the top electrode can influence leakage current characteristics of the Pt/SBT/Pt capacitor at positive voltage bias.展开更多
基金Supported by the National Natural Science Foundation of China under Grant Nos 90407023 and 60571009. The author would like to thank the Analysis and Test Centre in HUST for their help at FESEM and XRD testing.
文摘Conductive perovskite BaPb03 （BPO） films as a potential electrode material of PZT capacitors used in ferroelectric random access memory are prepared by rf magnetron sputtering. An x-ray diffractometer and standard four probe method are employed to investigate the dependence of growth conditions on crystal structure and conductivity of BPO films. It is found that BPO films with perovskite phase can be obtained at substrate temperatures above 425℃, and the sample with the lowest resistivity is obtained at 450℃ under pure argon atmosphere. Using this BPO film as electrode, ferroelectric properties of BPO/PZT/BPO and Pt/PZT/BPO sandwiched structures are evaluated. Their remanent polarization and coercive field are 36.6 ℃/cm^2 （81.3 k V/cm） and 36.9℃/cm^2 （89.1 kV/cm）, respectively. The coercive field of the former structure is lower than that of the latter, but remanent polarizations are almost the same. In addition, the results imply that BPO electrode is helpful to improve the fatigue resistance of PZT. The reasons are discussed.
基金Supported by the National Natural Science Foundation of China under Grant No 90407023, and the National High Technology Programme of China under Grant No 2004AA404240.
文摘We investigate SrBi2 Ta2 O9 （SBT） films prepared by the sol-gel spin method with different spin rates or different anneal conditions for the first layer of SBT, as promising ferroelectric layer materials applied to ferroelectric random access memory （FeRAM）. All the specimens in this experiment have similar SBT crystal orientations of （115）, （020）, （220）, and （135）. The Pt/SBT/Pt capacitor with coating of 3000rpm spin rate has a perfect rectangle shape of hysteresis loops, remanent polarization of 7.571μC/cm^2 and coercive voltage of 0.816 V at 5 V voltage amplitude. These characteristics are better than those with coating of 3500rpm spin rate, which is attributed to the influence for thickness and grain size of the film from depressed spin rate. Slow-rate anneal in the furnace for the first layer of SBT can improve the crystallization processes and properties for SBT layers slightly, compared with rapid thermal annealing. The ion damage from etching for the top electrode can influence leakage current characteristics of the Pt/SBT/Pt capacitor at positive voltage bias.