By using polarization resistance measurement and electrochemical impedance spectroscopy(EIS),in field corrosion electrochemical detections of Q235 carbon steel and Q235 ultrafine grained steel immersed samples in Zhou...By using polarization resistance measurement and electrochemical impedance spectroscopy(EIS),in field corrosion electrochemical detections of Q235 carbon steel and Q235 ultrafine grained steel immersed samples in Zhoushan Marine Corrosion Test Station were performed for 4 years.Dynamic corrosion data during exposure were obtained.Electrochemical detection results reflected not only the corrosion modalities and corrosion rates of the samples,but also the direct influence of marine environmental factors on the corrosion behavior.Seawater temperature was the major factor influencing the corrosion behaviors of carbon steels,and corrosion rates of these samples increased with increasing seawater temperature.The influence of seawater velocity and orientation of flow was less than that of temperature.展开更多
In this paper, with the technology of vacuum sputter, pure aluminum corrosion sensitive film was directly deposited on the core of optical fiber with its clad removed.Metallographic microscope and scanning electron mi...In this paper, with the technology of vacuum sputter, pure aluminum corrosion sensitive film was directly deposited on the core of optical fiber with its clad removed.Metallographic microscope and scanning electron microscope (SEM) were used to analyze the structure of the film.The thickness of the pure aluminum corrosion sensitive film was about 14.65 μm, and the film was distributed evenly and firmly bonded with the fiber core.Galvanostatic step and electrochemical impedance spectroscopy (EIS) were used to evaluate the corrosion resistance in NaCl solution with different concentrations (0.001—0.1 mol·L -1).The result showed that the corrosion resistance of the aluminum film was similar to that of industrial pure aluminum in NaCl solution with the concentration less than 0.1 mol·L -1.But the EIS data showed that there were holes on the film surface.展开更多
文摘By using polarization resistance measurement and electrochemical impedance spectroscopy(EIS),in field corrosion electrochemical detections of Q235 carbon steel and Q235 ultrafine grained steel immersed samples in Zhoushan Marine Corrosion Test Station were performed for 4 years.Dynamic corrosion data during exposure were obtained.Electrochemical detection results reflected not only the corrosion modalities and corrosion rates of the samples,but also the direct influence of marine environmental factors on the corrosion behavior.Seawater temperature was the major factor influencing the corrosion behaviors of carbon steels,and corrosion rates of these samples increased with increasing seawater temperature.The influence of seawater velocity and orientation of flow was less than that of temperature.
文摘In this paper, with the technology of vacuum sputter, pure aluminum corrosion sensitive film was directly deposited on the core of optical fiber with its clad removed.Metallographic microscope and scanning electron microscope (SEM) were used to analyze the structure of the film.The thickness of the pure aluminum corrosion sensitive film was about 14.65 μm, and the film was distributed evenly and firmly bonded with the fiber core.Galvanostatic step and electrochemical impedance spectroscopy (EIS) were used to evaluate the corrosion resistance in NaCl solution with different concentrations (0.001—0.1 mol·L -1).The result showed that the corrosion resistance of the aluminum film was similar to that of industrial pure aluminum in NaCl solution with the concentration less than 0.1 mol·L -1.But the EIS data showed that there were holes on the film surface.