Photorefractive properties of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording ...Photorefractive properties of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf:Fe:LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf:Fe:LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method for Hf:Fe:LiNbO3 crystal to improve its photorefractive properties.展开更多
The photochemical kinetics of phenanthrenequinone (PQ) doped poly (methyl methacrylate) photopolymer in holographic recording was studied theoretically and experimentally. The diffusion of PQ molecules during holograp...The photochemical kinetics of phenanthrenequinone (PQ) doped poly (methyl methacrylate) photopolymer in holographic recording was studied theoretically and experimentally. The diffusion of PQ molecules during holographic recording was negligible because of its small diffusion coefficient at room temperature. A photochemical reaction kinetics model of PQ/PMMA was established. The analytical expressions for the temporal variations of transmittance and diffraction efficiency were derived. By fitting the experimental curves, some parameters related with the polymer components were obtained by the proposed model, which can be used to analyze the photochemical process and will be helpful to the optimization of material preparation.展开更多
基金supported by the Fundamental Research Foundation of Commission of Science Technology,Industry for National Defense of China (Grant No.2320060089)and National Basic Research and Development Program of China (Grant No.2007CB3070001)Program of Excellent Team in Harbin Institute of Technology,China
文摘Photorefractive properties of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf:Fe:LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf:Fe:LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method for Hf:Fe:LiNbO3 crystal to improve its photorefractive properties.
基金Project supported by the Fundamental Research Foundation of COSTIND (Grant No 2320060089)the MOST of China (973 Project Grant No 2007CB307001)Program of Excellent Team in Harbin Institute of Technology
文摘The photochemical kinetics of phenanthrenequinone (PQ) doped poly (methyl methacrylate) photopolymer in holographic recording was studied theoretically and experimentally. The diffusion of PQ molecules during holographic recording was negligible because of its small diffusion coefficient at room temperature. A photochemical reaction kinetics model of PQ/PMMA was established. The analytical expressions for the temporal variations of transmittance and diffraction efficiency were derived. By fitting the experimental curves, some parameters related with the polymer components were obtained by the proposed model, which can be used to analyze the photochemical process and will be helpful to the optimization of material preparation.