Mg-Sn based alloy is one of the potential alloys for application at elevated temperature.The compressive creep behavior of ageing-treated Mg-xSn(x=3%,5%) alloys was investigated at the temperatures of 423 and 473 K an...Mg-Sn based alloy is one of the potential alloys for application at elevated temperature.The compressive creep behavior of ageing-treated Mg-xSn(x=3%,5%) alloys was investigated at the temperatures of 423 and 473 K and the stresses from 25 MPa to 35 MPa.When the tin content varies,the ageing-treated Mg-xSn alloys show quite different creep resistance,which are mainly attributed to the size and distribution of Mg_2Sn phases in the ageing-treated Mg-xSn alloys.The calculated value of stress exponent, n=6.3,suggests that the compressive creep behavior of the ageing-treated Mg-5%Sn alloy is controlled by dislocation creep at the temperature of 473 K and the stresses from 25 MPa to 35 MPa.展开更多
The microstructure,tensile properties and compressive creep resistance of permanent-mould cast Mg-(5-8.5)%Sn-2%La (mass fraction) alloys were investigated.The results show that Mg-(5-8.5)%Sn-2%La alloys are all compos...The microstructure,tensile properties and compressive creep resistance of permanent-mould cast Mg-(5-8.5)%Sn-2%La (mass fraction) alloys were investigated.The results show that Mg-(5-8.5)%Sn-2%La alloys are all composed ofα-Mg phase, Mg_2Sn and Mg-La-Sn compounds.Compared with those of Mg-5%Sn binary alloy,the grain size and the content of Mg_2Sn compound in Mg-5%Sn-2%La alloy are decreased.With the increase of Sn content in Mg-(5-8.5)%Sn-2%La alloys,the content of Mg_2Sn compound increases,while that of Mg-Sn-La compound changes little.In addition,the investigation suggests that the thermally stable Mg-Sn-La and Mg2Sn compounds can improve the tensile properties and compressive creep resistance of the alloys.展开更多
Microstructure, tensile properties and compressive creep behaviors of Mg-(1.65–11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper. The microstructure of the as-cast Mg-Sn-Nd alloys consisted of dendritic α-M...Microstructure, tensile properties and compressive creep behaviors of Mg-(1.65–11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper. The microstructure of the as-cast Mg-Sn-Nd alloys consisted of dendritic α-Mg, Mg2Sn and Mg-Sn-Nd ternary phase containing rare earth element. The highest ultimate tensile strength of 140 MPa and percentage elongation after fracture of 9.7%, were achieved with a composition of Mg-8.23 wt.% Sn-2 wt.% Nd. The compressive creep resistance of Mg-8.23 wt.%Sn-2 wt.% Nd alloy w...展开更多
文摘Mg-Sn based alloy is one of the potential alloys for application at elevated temperature.The compressive creep behavior of ageing-treated Mg-xSn(x=3%,5%) alloys was investigated at the temperatures of 423 and 473 K and the stresses from 25 MPa to 35 MPa.When the tin content varies,the ageing-treated Mg-xSn alloys show quite different creep resistance,which are mainly attributed to the size and distribution of Mg_2Sn phases in the ageing-treated Mg-xSn alloys.The calculated value of stress exponent, n=6.3,suggests that the compressive creep behavior of the ageing-treated Mg-5%Sn alloy is controlled by dislocation creep at the temperature of 473 K and the stresses from 25 MPa to 35 MPa.
文摘The microstructure,tensile properties and compressive creep resistance of permanent-mould cast Mg-(5-8.5)%Sn-2%La (mass fraction) alloys were investigated.The results show that Mg-(5-8.5)%Sn-2%La alloys are all composed ofα-Mg phase, Mg_2Sn and Mg-La-Sn compounds.Compared with those of Mg-5%Sn binary alloy,the grain size and the content of Mg_2Sn compound in Mg-5%Sn-2%La alloy are decreased.With the increase of Sn content in Mg-(5-8.5)%Sn-2%La alloys,the content of Mg_2Sn compound increases,while that of Mg-Sn-La compound changes little.In addition,the investigation suggests that the thermally stable Mg-Sn-La and Mg2Sn compounds can improve the tensile properties and compressive creep resistance of the alloys.
基金Project supported by the Science & Technology Bureau of Sichuan Province of China (03GG009-007-4)
文摘Microstructure, tensile properties and compressive creep behaviors of Mg-(1.65–11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper. The microstructure of the as-cast Mg-Sn-Nd alloys consisted of dendritic α-Mg, Mg2Sn and Mg-Sn-Nd ternary phase containing rare earth element. The highest ultimate tensile strength of 140 MPa and percentage elongation after fracture of 9.7%, were achieved with a composition of Mg-8.23 wt.% Sn-2 wt.% Nd. The compressive creep resistance of Mg-8.23 wt.%Sn-2 wt.% Nd alloy w...