The effects of high-volume slag-fly ash cement with different particle sizes on hydration degree,microstructure and mechanical properties were systematically studied,by means of laser particle size(DLS),X-ray diffract...The effects of high-volume slag-fly ash cement with different particle sizes on hydration degree,microstructure and mechanical properties were systematically studied,by means of laser particle size(DLS),X-ray diffraction (XRD),comprehensive thermal analysis (TG-DTA),scanning electron microscopy(SEM) and mechanical properties tests.The results show that suitable particle size distribution of cementitious material has significantly promoting effects on hydration reaction rate and mechanical properties.Compared with slag without further grinding,the slag after ball milling for 4 h has an obvious improvement in reactivity,which also provides a faster hydration rate and higher compressive strength for the cementitious material.When the slag milled for 1 and 4 h is mixed at a mass ratio of 2:1 (i e,slag with D_(50) of 7.4μm and average size of 9.9μm,and slag with D_(50) value of 2.6μm and average size of 5.3μm),and a certain amount of fly ash is added in,the most obvious improvement of compressive strength of cement is achieved.展开更多
基金Funded by the National Natural Science Foundation of China(No.52172025)。
文摘The effects of high-volume slag-fly ash cement with different particle sizes on hydration degree,microstructure and mechanical properties were systematically studied,by means of laser particle size(DLS),X-ray diffraction (XRD),comprehensive thermal analysis (TG-DTA),scanning electron microscopy(SEM) and mechanical properties tests.The results show that suitable particle size distribution of cementitious material has significantly promoting effects on hydration reaction rate and mechanical properties.Compared with slag without further grinding,the slag after ball milling for 4 h has an obvious improvement in reactivity,which also provides a faster hydration rate and higher compressive strength for the cementitious material.When the slag milled for 1 and 4 h is mixed at a mass ratio of 2:1 (i e,slag with D_(50) of 7.4μm and average size of 9.9μm,and slag with D_(50) value of 2.6μm and average size of 5.3μm),and a certain amount of fly ash is added in,the most obvious improvement of compressive strength of cement is achieved.