Polyaluminium chlorides with sulfate ion(PACS) were prepared by using AlCl 3·6H 2O, Al(SO 4) 3·18H 2O and Na 2CO 3 as raw materials. The effects of basicity ( r ), Al 3+ /SO 4 2- molar r...Polyaluminium chlorides with sulfate ion(PACS) were prepared by using AlCl 3·6H 2O, Al(SO 4) 3·18H 2O and Na 2CO 3 as raw materials. The effects of basicity ( r ), Al 3+ /SO 4 2- molar ratio and aging time on the morphology of PACS were observed by transmission electrical microscope. The influence of aging time on charge neutralization and coagulation effect of PACS was studied. The effects of basicity ( r ), Al 3+ /SO 4 2- molar ratio and aging time on the electrical conductivity of PACS solution were also investigated. The experimental results show that the degree of polymerization of polyaluminium chloride(PAC) increases when SO 4 2- ion is added. The higher the basicity( r ) and the longer the aging time, the larger the size of polymer PACS. The ability of PACS neutralizing the charge on Kaolinite decreases with the increase of aging time. The electrical conductivity of PACS solution(the concentration of Al 3+ ion is 0.18 mol/L) with different aging time is the function of the basicity and Al 3+ /SO 4 2- molar ratios and has its maximum at r =0.5 and Al 3+ /SO 4 2- =12.展开更多
文摘Polyaluminium chlorides with sulfate ion(PACS) were prepared by using AlCl 3·6H 2O, Al(SO 4) 3·18H 2O and Na 2CO 3 as raw materials. The effects of basicity ( r ), Al 3+ /SO 4 2- molar ratio and aging time on the morphology of PACS were observed by transmission electrical microscope. The influence of aging time on charge neutralization and coagulation effect of PACS was studied. The effects of basicity ( r ), Al 3+ /SO 4 2- molar ratio and aging time on the electrical conductivity of PACS solution were also investigated. The experimental results show that the degree of polymerization of polyaluminium chloride(PAC) increases when SO 4 2- ion is added. The higher the basicity( r ) and the longer the aging time, the larger the size of polymer PACS. The ability of PACS neutralizing the charge on Kaolinite decreases with the increase of aging time. The electrical conductivity of PACS solution(the concentration of Al 3+ ion is 0.18 mol/L) with different aging time is the function of the basicity and Al 3+ /SO 4 2- molar ratios and has its maximum at r =0.5 and Al 3+ /SO 4 2- =12.