The leaching of cobalt from four-mixed Co-Cu oxidized ores containing cobalt at levels ranging from 0.5wt% to 34wt% was studied and the results has been reported. Conventional dissolution of these oxidized Co-Cu ores ...The leaching of cobalt from four-mixed Co-Cu oxidized ores containing cobalt at levels ranging from 0.5wt% to 34wt% was studied and the results has been reported. Conventional dissolution of these oxidized Co-Cu ores with diluted H2SO4 and SO2 as a reducing agent resulted in a substantial improvement in the solution based recovery of cobalt. UV/visible spectroscopic analysis of the leached solu-tions indicated that the increased cobalt content in the solution was a result of flushing the acidified cobalt leaching solution with SO2. Fur-thermore, UV/visible spectroscopy confirmed that as SO2 was flushed into the acidified leaching solution, Co3＋ bearing minerals were re-duced to the readily soluble Co2＋ bearing minerals, and this resulted in the increase of total cobalt in the collected solution. The mechanism of the reduction of Co3＋ to Co2＋ bearing minerals when SO2 is flushed during the leaching of mixed Co-Cu oxidized ores, including the stability trends of Co3＋, Co2＋, and Cu2＋ complexes, as shown by their UV/visible spectra, are also discussed.展开更多
文摘The leaching of cobalt from four-mixed Co-Cu oxidized ores containing cobalt at levels ranging from 0.5wt% to 34wt% was studied and the results has been reported. Conventional dissolution of these oxidized Co-Cu ores with diluted H2SO4 and SO2 as a reducing agent resulted in a substantial improvement in the solution based recovery of cobalt. UV/visible spectroscopic analysis of the leached solu-tions indicated that the increased cobalt content in the solution was a result of flushing the acidified cobalt leaching solution with SO2. Fur-thermore, UV/visible spectroscopy confirmed that as SO2 was flushed into the acidified leaching solution, Co3＋ bearing minerals were re-duced to the readily soluble Co2＋ bearing minerals, and this resulted in the increase of total cobalt in the collected solution. The mechanism of the reduction of Co3＋ to Co2＋ bearing minerals when SO2 is flushed during the leaching of mixed Co-Cu oxidized ores, including the stability trends of Co3＋, Co2＋, and Cu2＋ complexes, as shown by their UV/visible spectra, are also discussed.
