Glasses with chemical composition of (in mol.%): 26 RF-20 PbO-10 TeO2-43 H3BO3-1 EuO3 (RLTB) were prepared by conventional melt quenching method. The Judd-Ofelt intensity parameters Ω2 and Ω6 were obtained from the ...Glasses with chemical composition of (in mol.%): 26 RF-20 PbO-10 TeO2-43 H3BO3-1 EuO3 (RLTB) were prepared by conventional melt quenching method. The Judd-Ofelt intensity parameters Ω2 and Ω6 were obtained from the absorption intensities of 7F0→5D2 and 7F0→5L6 transitions, respectively. In order to overcome the problem of applicability of Judd-Ofelt analysis at room temperature due to the overlapping of the transitions originating from 7F0 and 7F1 levels of Eu3+ ion, the effect of the thermalization on the ...展开更多
基金supported by the Defence Research and Development Organisation,New Delhi (ERIP/RE/0603593/M/01/984)
文摘Glasses with chemical composition of (in mol.%): 26 RF-20 PbO-10 TeO2-43 H3BO3-1 EuO3 (RLTB) were prepared by conventional melt quenching method. The Judd-Ofelt intensity parameters Ω2 and Ω6 were obtained from the absorption intensities of 7F0→5D2 and 7F0→5L6 transitions, respectively. In order to overcome the problem of applicability of Judd-Ofelt analysis at room temperature due to the overlapping of the transitions originating from 7F0 and 7F1 levels of Eu3+ ion, the effect of the thermalization on the ...