Al–Si–Cu–Mg foundry alloys are used in casting process technologies.However,their strength properties remain low due to their microstructural characteristics and porosity.In this work,the microstructural characteri...Al–Si–Cu–Mg foundry alloys are used in casting process technologies.However,their strength properties remain low due to their microstructural characteristics and porosity.In this work,the microstructural characteristics,dislocation densities,and mechanical properties of Al–Si–Cu–Mg cast alloys prepared through different casting methods were studied experimentally.Four casting processes,namely,gravity casting(GC),rheocasting(RC),thixoforming(Thixo),and Thixo with heat treatment,were used.The GC and RC samples had mainly dendriticα-Al phase microstructures and exhibited coarse Si particles and intermetallic compounds in their interdendritic regions.By contrast,the Thixo and heat-treated Thixo(HT-Thixo)samples exhibited microstructural refinement with uniformly distributedα-Al globules,fine fibrous Si particles,and fragmented intermetallic compounds amongα-Al globules.The accumulation of dislocation densities increased in the Thixo sample as the strain was increased due to plastic deformation.Furthermore,the ultimate tensile strength and yield strength of the HT-Thixo sample increased by 87%and 63%,respectively,relative to those of the GC sample.The cleavage fracture displayed by the GC and RC samples led to brittle failure.Meanwhile,the Thixo and HT-Thixo samples presented dimple-based ductile fracture.展开更多
基金financially supported by the Universiti Kebangsaan Malaysia and the Ministry of Education(MoE)Malaysia(Nos.MI-2019-025 and DIP-2016-007)。
文摘Al–Si–Cu–Mg foundry alloys are used in casting process technologies.However,their strength properties remain low due to their microstructural characteristics and porosity.In this work,the microstructural characteristics,dislocation densities,and mechanical properties of Al–Si–Cu–Mg cast alloys prepared through different casting methods were studied experimentally.Four casting processes,namely,gravity casting(GC),rheocasting(RC),thixoforming(Thixo),and Thixo with heat treatment,were used.The GC and RC samples had mainly dendriticα-Al phase microstructures and exhibited coarse Si particles and intermetallic compounds in their interdendritic regions.By contrast,the Thixo and heat-treated Thixo(HT-Thixo)samples exhibited microstructural refinement with uniformly distributedα-Al globules,fine fibrous Si particles,and fragmented intermetallic compounds amongα-Al globules.The accumulation of dislocation densities increased in the Thixo sample as the strain was increased due to plastic deformation.Furthermore,the ultimate tensile strength and yield strength of the HT-Thixo sample increased by 87%and 63%,respectively,relative to those of the GC sample.The cleavage fracture displayed by the GC and RC samples led to brittle failure.Meanwhile,the Thixo and HT-Thixo samples presented dimple-based ductile fracture.