The mixed spinel ferrite system Mg0.95Mn0.05Fe2-2xTi2xO4(0≤x≤0.7) was synthesized by the conventional solid-state reaction technique.The effect of Ti4+ doping was studied by using the Mssbauer spectroscopy measure...The mixed spinel ferrite system Mg0.95Mn0.05Fe2-2xTi2xO4(0≤x≤0.7) was synthesized by the conventional solid-state reaction technique.The effect of Ti4+ doping was studied by using the Mssbauer spectroscopy measurements at room temperature.From the analysis of the Mssbauer spectra,it is observed that s-electron density,electric field gradient(EFG),quadrupole coupling constant(QCC) and the net hyperfine magnetic fields acting on the M-ssbauer nuclei-FeA3+ and FeB3+ change with the increase of Ti4+ doping in Mg0.95Mn0.05Fe2O4.The hyperfine magnetic field decreases with the increase of Ti4+ doping.展开更多
The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,i...The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,it is observed that the resolved hyperfine sextets are due to the distribution of Fe ions on the two sublattices of the spinel ferrites.The value of the isomer shift obtained from the fitting of the Mssbauer spectra indicates that Fe ions are in +3 state.A paramagnetic doublet is observed at degree of inversion x=0.4,superimposed on the hyperfine sextets,indicating that the super-exchange interaction A-B decreases due to the dilution of sublattice by Al3+ ions.The hyperfine magnetic field decreases at both interstitial sites of tetrahedral(A) and octahedral(B) with the increase in Al concentration.展开更多
基金Project supported by the Second Stage of Brain Korea 21 ProjectProject(RTI04-01-03) supported by the Regional Technology Innovation Program of the Ministry of Knowledge Economy (MKE),Korea
文摘The mixed spinel ferrite system Mg0.95Mn0.05Fe2-2xTi2xO4(0≤x≤0.7) was synthesized by the conventional solid-state reaction technique.The effect of Ti4+ doping was studied by using the Mssbauer spectroscopy measurements at room temperature.From the analysis of the Mssbauer spectra,it is observed that s-electron density,electric field gradient(EFG),quadrupole coupling constant(QCC) and the net hyperfine magnetic fields acting on the M-ssbauer nuclei-FeA3+ and FeB3+ change with the increase of Ti4+ doping in Mg0.95Mn0.05Fe2O4.The hyperfine magnetic field decreases with the increase of Ti4+ doping.
基金Project supported by the Second Stage of Brain Korea 21 ProjectProject(RTI04-01-03) supported by the Regional Technology Innovation Program of the Ministry of Knowledge Economy (MKE),Korea
文摘The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,it is observed that the resolved hyperfine sextets are due to the distribution of Fe ions on the two sublattices of the spinel ferrites.The value of the isomer shift obtained from the fitting of the Mssbauer spectra indicates that Fe ions are in +3 state.A paramagnetic doublet is observed at degree of inversion x=0.4,superimposed on the hyperfine sextets,indicating that the super-exchange interaction A-B decreases due to the dilution of sublattice by Al3+ ions.The hyperfine magnetic field decreases at both interstitial sites of tetrahedral(A) and octahedral(B) with the increase in Al concentration.