Dissolution kinetics of nickel from lateritic ore in nitric acid solution was investigated. Experimental parameters used were stirring speed(100-600 r/min), temperature(40-96 °C), nitric acid concentration(0.1-2 ...Dissolution kinetics of nickel from lateritic ore in nitric acid solution was investigated. Experimental parameters used were stirring speed(100-600 r/min), temperature(40-96 °C), nitric acid concentration(0.1-2 mol/L) and particle size(<106 μm). The shrinking core model was applied to the results of experiments investigating the effects of leaching temperature in the range of 40-90 °C and nitric acid concentration in range of 0.1-2 mol/L on nickel dissolution rate. The kinetic analysis shows that the nickel dissolution from lateritic ore could be described by diffusion model. The activation energy(E_a) for the dissolution reaction is calculated as 79.52 kJ/mol.展开更多
基金supported by The Research Foundation of the Selcuk University under the Project No:06101021
文摘Dissolution kinetics of nickel from lateritic ore in nitric acid solution was investigated. Experimental parameters used were stirring speed(100-600 r/min), temperature(40-96 °C), nitric acid concentration(0.1-2 mol/L) and particle size(<106 μm). The shrinking core model was applied to the results of experiments investigating the effects of leaching temperature in the range of 40-90 °C and nitric acid concentration in range of 0.1-2 mol/L on nickel dissolution rate. The kinetic analysis shows that the nickel dissolution from lateritic ore could be described by diffusion model. The activation energy(E_a) for the dissolution reaction is calculated as 79.52 kJ/mol.