The nanocomposite of MoSi2-SiaN4 （molybdenum disilicide-silicon nitride） was synthesized by reaction milling of the Mo and Si powder mixture. Changing the processing parameters led to the formation of different prod...The nanocomposite of MoSi2-SiaN4 （molybdenum disilicide-silicon nitride） was synthesized by reaction milling of the Mo and Si powder mixture. Changing the processing parameters led to the formation of different products such as a- and B-MoSi2, SiaN4, Mo2N, and M05Si3 at various milling times. A thermodynamic appraisal showed that the milling of Moa2Siss powder mixture was associated with highly exothermic mechanically induced self-sustaining reaction （MSR） between Mo and Si. The MSR took place around 5 h of milling led to the formation of a-MoSi2 and the reaction between Si and N2 to produce Si3N4 under a nitrogen pressure of 1 MPa. By increasing the nitrogen pressure to 5 MPa, more heat is released, resulting in the dissociation of Si3N4 and the transformation of a-MoSi2 to β-MoSi2. Heat treatment was also performed on the milled samples and led to the formation of Mo2N and the transformation of a-MoSi2 to β-MoSi2 at the milling times of 10 and 40 h, respectively.展开更多
文摘The nanocomposite of MoSi2-SiaN4 （molybdenum disilicide-silicon nitride） was synthesized by reaction milling of the Mo and Si powder mixture. Changing the processing parameters led to the formation of different products such as a- and B-MoSi2, SiaN4, Mo2N, and M05Si3 at various milling times. A thermodynamic appraisal showed that the milling of Moa2Siss powder mixture was associated with highly exothermic mechanically induced self-sustaining reaction （MSR） between Mo and Si. The MSR took place around 5 h of milling led to the formation of a-MoSi2 and the reaction between Si and N2 to produce Si3N4 under a nitrogen pressure of 1 MPa. By increasing the nitrogen pressure to 5 MPa, more heat is released, resulting in the dissociation of Si3N4 and the transformation of a-MoSi2 to β-MoSi2. Heat treatment was also performed on the milled samples and led to the formation of Mo2N and the transformation of a-MoSi2 to β-MoSi2 at the milling times of 10 and 40 h, respectively.