In the present study,we have synthesized polycrystalline samples of BaTi_(1-x)Co_(x)O_(3)(BTCO)(x=0,0.01,0.03,0.05,0.07 and 0.10)with standard solid state reaction technique.The obtained samples are characterized by X...In the present study,we have synthesized polycrystalline samples of BaTi_(1-x)Co_(x)O_(3)(BTCO)(x=0,0.01,0.03,0.05,0.07 and 0.10)with standard solid state reaction technique.The obtained samples are characterized by X-ray diffraction(XRD)and Raman spectroscopy for structural study.The detailed structural analysis has been performed by Rietveld refinement using Fullprof program.We observed an increase in lattice parameters,which results due to substitution of Co2t with large ionic radii(0.9Å)for smaller ionic radii(0.6Å)Ti4t.Moreover,peak at 45.5°shifts to 45°on Co doping,which is due to structure phase transition from tetragonal to cubic.Raman study infers that the intensity of characteristic peaks decreases and line width increases with Co doping.The bands linked with the tetragonal structure(305 cm1)decreased due to the tetragonal-to-cubic phase transition with Co doping.Our structural study reveals the expansion of BTCO unit cell and tetragonal-to-cubic phase transformation takes place.The results from different characterization techniques are conclusive and show structural evolution with Co doping.The samples are further characterized by dielectric spectroscopy,dielectric measurement reveals the increase of dielectric constant and transition T_(c)-125° is observed for Barium titanate(BaTiO3),whereas transition disappears with Co doping.Both temperature and frequency-dependent tangent loss is also studied.展开更多
文摘In the present study,we have synthesized polycrystalline samples of BaTi_(1-x)Co_(x)O_(3)(BTCO)(x=0,0.01,0.03,0.05,0.07 and 0.10)with standard solid state reaction technique.The obtained samples are characterized by X-ray diffraction(XRD)and Raman spectroscopy for structural study.The detailed structural analysis has been performed by Rietveld refinement using Fullprof program.We observed an increase in lattice parameters,which results due to substitution of Co2t with large ionic radii(0.9Å)for smaller ionic radii(0.6Å)Ti4t.Moreover,peak at 45.5°shifts to 45°on Co doping,which is due to structure phase transition from tetragonal to cubic.Raman study infers that the intensity of characteristic peaks decreases and line width increases with Co doping.The bands linked with the tetragonal structure(305 cm1)decreased due to the tetragonal-to-cubic phase transition with Co doping.Our structural study reveals the expansion of BTCO unit cell and tetragonal-to-cubic phase transformation takes place.The results from different characterization techniques are conclusive and show structural evolution with Co doping.The samples are further characterized by dielectric spectroscopy,dielectric measurement reveals the increase of dielectric constant and transition T_(c)-125° is observed for Barium titanate(BaTiO3),whereas transition disappears with Co doping.Both temperature and frequency-dependent tangent loss is also studied.