Effects of specific surface area and tiny amount of impurities of reactive alumina on the workability, sinte- ring and high temperature mechanical strength of corun- dum based castables were investigated. The results ...Effects of specific surface area and tiny amount of impurities of reactive alumina on the workability, sinte- ring and high temperature mechanical strength of corun- dum based castables were investigated. The results show that the presence of reactive alumina with high specific surface area leads to accelerating of the hydration of calcium aluminate cement, thus shortening the working time and setting time of the castables, which can be as- cribed that the critical energy barrier for stable nuclei of hydration products of cement can be reduced by the high specific surface area of reactive alumina. The sintering of the corundum based castables can be accelerated by the reactive alumina with high specific surface area and high amount of impurities, however, the reactive alumina with too high specific surface area and impurities can al- so lead to noticeable shrinkage of castables. In addition, high temperature mechanical strength of corundum based castables can be decreased by the higher amount of trace impurities of reactive alumina due to formation of low- melting phase at high temperatures.展开更多
The paper discusses the difference in the formulation concepts of alumina - spinel （spinel containing ） and alumina - magnesia （ spin, el forming） castables and the influence on their physical properties. The indi...The paper discusses the difference in the formulation concepts of alumina - spinel （spinel containing ） and alumina - magnesia （ spin, el forming） castables and the influence on their physical properties. The individual property profile is discussed with respect to the requirements of refactory lining materials for the different zones of a steel ladle.展开更多
Historically,ground calcined aluminas were the first high-alumina matrix products that were used in refractory formulations, in both shaped and unshaped products. At that time the flow properties of castables were enh...Historically,ground calcined aluminas were the first high-alumina matrix products that were used in refractory formulations, in both shaped and unshaped products. At that time the flow properties of castables were enhanced by the use of silica fume. This was followed later by the development of fully ground reactive aluminas which contributed to the design of the matrix below 63 μm. In addition to aggregate fines,a range of bi-modal and multi-modal reactive aluminas were also developed. These not only gave improved physical properties but also better castable workability. This paper reviews matrix alumina developments over time,from basic ground calcines to complex multi-modal matrix products and their globally standardised manufacture.展开更多
Purging plugs installed in the bottom of steel ladles are widely used for the secondary refining of high quality steel grades.The dynamic service conditions and temperature gradients caused by the cold inert gas blown...Purging plugs installed in the bottom of steel ladles are widely used for the secondary refining of high quality steel grades.The dynamic service conditions and temperature gradients caused by the cold inert gas blown through the plug during stirring create a strong thermal shock impact on the materials.This can affect its service life and restrict the safety and efficiency of steel making if the plug fails during use.In this work,the influence of the particle size distribution (PSD) and amount of reactive alumina on the sintering behavior of ultra-low cement bonded corundum-spinel based castables was investigated on lab scale.The relationship between sintering reactivity of matrix and thermal shock resistance of castables was evaluated in detail.Results show that the sintering of castables can be intensified by using finer reactive alumina.However,excessive sintering of the castable through finer reactive alumina is negative for thermal shock resistance.The microstructure characterization reveals that castables with more intense sintering show denser matrix structure,which is less effective in hampering crack propagation and therefore results in decline of their thermal shock resistance.展开更多
Three different castables based on the Al_2O_3–MgO –CaO system were prepared as steel-ladle purging plug refractories： corundum-based low-cement castable（C-LCC）, corundum-spinel-based low-cement castable（C-S-LCC...Three different castables based on the Al_2O_3–MgO –CaO system were prepared as steel-ladle purging plug refractories： corundum-based low-cement castable（C-LCC）, corundum-spinel-based low-cement castable（C-S-LCC）, and corundum-spinel no-cement castable（C-S-NCC）（hydratable alumina（ρ-Al_2O_3） bonded）. The fracture behavior at room temperature was tested by the method of ＂wedge-splitting＂ on samples pre-fired at different temperatures; the specific fracture energy G′f and notched tensile strength σNT were obtained from these tests. In addition, the Young＇s modulus E was measured by the method of resonance frequency of damping analysis（RFDA）. The thermal stress resistance parameter R′′′′ calculated using the values of G′f, σNT, and E was used to evaluate the thermal shock resistance of the materials. According to the microstructure analysis results, the sintering effect and the bonding type of the matrix material were different among these three castables, which explains their different fracture behaviors.展开更多
文摘Effects of specific surface area and tiny amount of impurities of reactive alumina on the workability, sinte- ring and high temperature mechanical strength of corun- dum based castables were investigated. The results show that the presence of reactive alumina with high specific surface area leads to accelerating of the hydration of calcium aluminate cement, thus shortening the working time and setting time of the castables, which can be as- cribed that the critical energy barrier for stable nuclei of hydration products of cement can be reduced by the high specific surface area of reactive alumina. The sintering of the corundum based castables can be accelerated by the reactive alumina with high specific surface area and high amount of impurities, however, the reactive alumina with too high specific surface area and impurities can al- so lead to noticeable shrinkage of castables. In addition, high temperature mechanical strength of corundum based castables can be decreased by the higher amount of trace impurities of reactive alumina due to formation of low- melting phase at high temperatures.
文摘The paper discusses the difference in the formulation concepts of alumina - spinel （spinel containing ） and alumina - magnesia （ spin, el forming） castables and the influence on their physical properties. The individual property profile is discussed with respect to the requirements of refactory lining materials for the different zones of a steel ladle.
文摘Historically,ground calcined aluminas were the first high-alumina matrix products that were used in refractory formulations, in both shaped and unshaped products. At that time the flow properties of castables were enhanced by the use of silica fume. This was followed later by the development of fully ground reactive aluminas which contributed to the design of the matrix below 63 μm. In addition to aggregate fines,a range of bi-modal and multi-modal reactive aluminas were also developed. These not only gave improved physical properties but also better castable workability. This paper reviews matrix alumina developments over time,from basic ground calcines to complex multi-modal matrix products and their globally standardised manufacture.
基金the National Natural Science Foundation of China(51572244 and U1604252)for supporting this work
文摘Purging plugs installed in the bottom of steel ladles are widely used for the secondary refining of high quality steel grades.The dynamic service conditions and temperature gradients caused by the cold inert gas blown through the plug during stirring create a strong thermal shock impact on the materials.This can affect its service life and restrict the safety and efficiency of steel making if the plug fails during use.In this work,the influence of the particle size distribution (PSD) and amount of reactive alumina on the sintering behavior of ultra-low cement bonded corundum-spinel based castables was investigated on lab scale.The relationship between sintering reactivity of matrix and thermal shock resistance of castables was evaluated in detail.Results show that the sintering of castables can be intensified by using finer reactive alumina.However,excessive sintering of the castable through finer reactive alumina is negative for thermal shock resistance.The microstructure characterization reveals that castables with more intense sintering show denser matrix structure,which is less effective in hampering crack propagation and therefore results in decline of their thermal shock resistance.
文摘Three different castables based on the Al_2O_3–MgO –CaO system were prepared as steel-ladle purging plug refractories： corundum-based low-cement castable（C-LCC）, corundum-spinel-based low-cement castable（C-S-LCC）, and corundum-spinel no-cement castable（C-S-NCC）（hydratable alumina（ρ-Al_2O_3） bonded）. The fracture behavior at room temperature was tested by the method of ＂wedge-splitting＂ on samples pre-fired at different temperatures; the specific fracture energy G′f and notched tensile strength σNT were obtained from these tests. In addition, the Young＇s modulus E was measured by the method of resonance frequency of damping analysis（RFDA）. The thermal stress resistance parameter R′′′′ calculated using the values of G′f, σNT, and E was used to evaluate the thermal shock resistance of the materials. According to the microstructure analysis results, the sintering effect and the bonding type of the matrix material were different among these three castables, which explains their different fracture behaviors.