This paper shows the results of the assessment of impairment suffered by elements of electronic equipment by environmental effects in different climatic zones of Mexico. For this study, evaluated devices were evaluate...This paper shows the results of the assessment of impairment suffered by elements of electronic equipment by environmental effects in different climatic zones of Mexico. For this study, evaluated devices were evaluated that are mostly exposed under different climatic conditions of operation, to determine the degree of damage suffered which leads to malfunction, reduced service life and loss of information in some cases. The main contribution is to identify the causes of the deterioration to delay the effect of atmospheric corrosion deterioration in electronic components. The Mexican Republic has a wide range of climates and subclimates over its territory, sampling was performed for each one of the most representative regions, by their nature tend to be more conducive to the release of corrosive effect on the computer and electronic devices. For the determination of existing impairment in electronic equipment, a methodology is proposed for the evaluation of samples taken from each region, determining the degree of corrosion that exists in these devices. It should be noted that according to the literature, the main pollutants that lead to the deterioration caused by corrosive environmental phenomena are SO2, NOx, CO, CO2, coupled with the presence of ozone and chloride, characteristic of the coastal region, combined with the percent relative humidity (% HR), and temperature cycles as reported by environmental monitoring systems in Mexico. With the study of atmospheric corrosivity in electronic devices has been determined: 1) Design and operation of chamber to accelerated atmospheric corrosion testing. 2) Identification of electronic components with increased susceptibility to corrosive phenomena under typical environmental different regions of Mexico. 3) Correlation of damage suffered in electronic equipment under typical operating conditions and accelerated tests. 4) Determining the degree of atmospheric corrosion on electronic equipment. 5) Construction of atmospheric corrosivity map for Mexico in electronic devices.展开更多
文摘This paper shows the results of the assessment of impairment suffered by elements of electronic equipment by environmental effects in different climatic zones of Mexico. For this study, evaluated devices were evaluated that are mostly exposed under different climatic conditions of operation, to determine the degree of damage suffered which leads to malfunction, reduced service life and loss of information in some cases. The main contribution is to identify the causes of the deterioration to delay the effect of atmospheric corrosion deterioration in electronic components. The Mexican Republic has a wide range of climates and subclimates over its territory, sampling was performed for each one of the most representative regions, by their nature tend to be more conducive to the release of corrosive effect on the computer and electronic devices. For the determination of existing impairment in electronic equipment, a methodology is proposed for the evaluation of samples taken from each region, determining the degree of corrosion that exists in these devices. It should be noted that according to the literature, the main pollutants that lead to the deterioration caused by corrosive environmental phenomena are SO2, NOx, CO, CO2, coupled with the presence of ozone and chloride, characteristic of the coastal region, combined with the percent relative humidity (% HR), and temperature cycles as reported by environmental monitoring systems in Mexico. With the study of atmospheric corrosivity in electronic devices has been determined: 1) Design and operation of chamber to accelerated atmospheric corrosion testing. 2) Identification of electronic components with increased susceptibility to corrosive phenomena under typical environmental different regions of Mexico. 3) Correlation of damage suffered in electronic equipment under typical operating conditions and accelerated tests. 4) Determining the degree of atmospheric corrosion on electronic equipment. 5) Construction of atmospheric corrosivity map for Mexico in electronic devices.
