Barium hexaferrites BaFe11.6Mox Zn0.4-x O19（x=0.1,0.2,0.4）were prepared by precipitation of the precursors using wet chemical mixture method and then sintering the dried powders at 1100℃.The properties of the prepa...Barium hexaferrites BaFe11.6Mox Zn0.4-x O19（x=0.1,0.2,0.4）were prepared by precipitation of the precursors using wet chemical mixture method and then sintering the dried powders at 1100℃.The properties of the prepared samples were investigated using X-ray difraction（XRD）,scanning electron microscopy（SEM）,vibrating sample magnetometer,and Mssbauer spectroscopy.XRD patterns revealed that all prepared samples had BaFe12O19hexaferrite structure as a majority phase.SEM images demonstated that the samples consisted mainly of hexagonal platelet-like grains with diameters ranging from 100 to 500 nm.Mssbauer spectra revealed that Zn2＋ions occupy 4f1 sites leading to the splitting of the 12k component.However Mo6＋ions occupy 2b sites while Mo4＋ prefer 4f1 and 12k sites.For the sample with x=0.4,Mo6＋and Mo4＋ ions were found to have preference for 2b and 12k sites,respectively,and to induce the development of Fe2＋ions in the hexaferrite,leading to noticeable changes in the magnetic properties of the system.The observed magnetic properties were found to be consistent with the preferential site occupation of metal ions,and the hyperfine fields derived from Mssbauer spectra of these samples.展开更多
基金supported by a generous grant from the Scientific Research Fund (SRF) in Jordan under grant number(S/1/21/2009)support of the German Academic Exchange Program(DAAD)the Deanship of Scientific research at the University of Jordan under contract number 1404 are also acknowledged
文摘Barium hexaferrites BaFe11.6Mox Zn0.4-x O19（x=0.1,0.2,0.4）were prepared by precipitation of the precursors using wet chemical mixture method and then sintering the dried powders at 1100℃.The properties of the prepared samples were investigated using X-ray difraction（XRD）,scanning electron microscopy（SEM）,vibrating sample magnetometer,and Mssbauer spectroscopy.XRD patterns revealed that all prepared samples had BaFe12O19hexaferrite structure as a majority phase.SEM images demonstated that the samples consisted mainly of hexagonal platelet-like grains with diameters ranging from 100 to 500 nm.Mssbauer spectra revealed that Zn2＋ions occupy 4f1 sites leading to the splitting of the 12k component.However Mo6＋ions occupy 2b sites while Mo4＋ prefer 4f1 and 12k sites.For the sample with x=0.4,Mo6＋and Mo4＋ ions were found to have preference for 2b and 12k sites,respectively,and to induce the development of Fe2＋ions in the hexaferrite,leading to noticeable changes in the magnetic properties of the system.The observed magnetic properties were found to be consistent with the preferential site occupation of metal ions,and the hyperfine fields derived from Mssbauer spectra of these samples.