The complex impedance spectroscopy and surface morphology of Mn1+xFe2-2xTixO4(0≤x≤0.5) system,prepared using a conventional solid state reaction technique,were investigated.The impedance spectroscopy measurements we...The complex impedance spectroscopy and surface morphology of Mn1+xFe2-2xTixO4(0≤x≤0.5) system,prepared using a conventional solid state reaction technique,were investigated.The impedance spectroscopy measurements were carried out at room temperature in the frequency range of 42-5 MHz.The electrical processes in the samples were modeled in the form of an equivalent circuit made up of a combination of two parallel RC circuits attributed to grain and grain boundaries.The DC conductivity obtained by extrapolation of AC data using impedance spectroscopy and four-probe method increases at 10% doping of Ti ions.The energy-dispersive X-ray(EDX) pattern confirmed the homogeneous mixing of the Mn,Fe,Ti and O atoms in pure and doped ferrite samples.展开更多
The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,i...The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,it is observed that the resolved hyperfine sextets are due to the distribution of Fe ions on the two sublattices of the spinel ferrites.The value of the isomer shift obtained from the fitting of the Mssbauer spectra indicates that Fe ions are in +3 state.A paramagnetic doublet is observed at degree of inversion x=0.4,superimposed on the hyperfine sextets,indicating that the super-exchange interaction A-B decreases due to the dilution of sublattice by Al3+ ions.The hyperfine magnetic field decreases at both interstitial sites of tetrahedral(A) and octahedral(B) with the increase in Al concentration.展开更多
基金Project supported by the Second Stage of Brain Korea 21 ProjectProject(RTI04-01-03) supported by the Regional Technology Innovation Program of the Ministry of Knowledge Economy (MKE),Korea
文摘The complex impedance spectroscopy and surface morphology of Mn1+xFe2-2xTixO4(0≤x≤0.5) system,prepared using a conventional solid state reaction technique,were investigated.The impedance spectroscopy measurements were carried out at room temperature in the frequency range of 42-5 MHz.The electrical processes in the samples were modeled in the form of an equivalent circuit made up of a combination of two parallel RC circuits attributed to grain and grain boundaries.The DC conductivity obtained by extrapolation of AC data using impedance spectroscopy and four-probe method increases at 10% doping of Ti ions.The energy-dispersive X-ray(EDX) pattern confirmed the homogeneous mixing of the Mn,Fe,Ti and O atoms in pure and doped ferrite samples.
基金Project supported by the Second Stage of Brain Korea 21 ProjectProject(RTI04-01-03) supported by the Regional Technology Innovation Program of the Ministry of Knowledge Economy (MKE),Korea
文摘The effect of non-magnetic Al3+ ion doping on the magnetic properties of MnFe2-2xAl2xO4(0≤x≤0.4) spinel ferrites was studied using Mssbauer spectroscopy measurements at room temperature.From the Mssbauer study,it is observed that the resolved hyperfine sextets are due to the distribution of Fe ions on the two sublattices of the spinel ferrites.The value of the isomer shift obtained from the fitting of the Mssbauer spectra indicates that Fe ions are in +3 state.A paramagnetic doublet is observed at degree of inversion x=0.4,superimposed on the hyperfine sextets,indicating that the super-exchange interaction A-B decreases due to the dilution of sublattice by Al3+ ions.The hyperfine magnetic field decreases at both interstitial sites of tetrahedral(A) and octahedral(B) with the increase in Al concentration.