A series of phosphine oxide-functionalized polyfluorene derivatives,PFH-PO-40-1 (P1),PFH-PO-20-1 (P2),PFH-PO-10-1 (P3),and PFH-PO-1-1 (P4),were prepared via a palladium-mediated Suzuki cross-coupling reaction.The stru...A series of phosphine oxide-functionalized polyfluorene derivatives,PFH-PO-40-1 (P1),PFH-PO-20-1 (P2),PFH-PO-10-1 (P3),and PFH-PO-1-1 (P4),were prepared via a palladium-mediated Suzuki cross-coupling reaction.The structures and purities of all polymers were fully characterized by 1H and 13C NMR,UV-vis and photoluminescent spectroscopy,gel permeation chromatography,and TGA/DSC.Their emission features showed single broad peaks at about 445 nm in film,compared with those in dilute solutions,which might be caused by some degree of aggregation in the excited states of the backbones.The best electroluminescence (EL) performance of these polymers with configuration of ITO/PEDOT:PSS/Polymer/Alq3/LiF/Al was obtained from P1 (current efficiency was 4.2 Cd/A at 6V).展开更多
基金supported by the National Basic Research Program of China (2006CB921602 and 2009CB623601)National Natural Science Foundation of China,and Hewlett Packard Company
文摘A series of phosphine oxide-functionalized polyfluorene derivatives,PFH-PO-40-1 (P1),PFH-PO-20-1 (P2),PFH-PO-10-1 (P3),and PFH-PO-1-1 (P4),were prepared via a palladium-mediated Suzuki cross-coupling reaction.The structures and purities of all polymers were fully characterized by 1H and 13C NMR,UV-vis and photoluminescent spectroscopy,gel permeation chromatography,and TGA/DSC.Their emission features showed single broad peaks at about 445 nm in film,compared with those in dilute solutions,which might be caused by some degree of aggregation in the excited states of the backbones.The best electroluminescence (EL) performance of these polymers with configuration of ITO/PEDOT:PSS/Polymer/Alq3/LiF/Al was obtained from P1 (current efficiency was 4.2 Cd/A at 6V).