In this work,a novel coating with a non-antibiotic agent for inhibiting Gram-positive bacteria and promoting osteogenesis was prepared on zinc-aluminium alloy(ZA6-1)via mussel mimetic polydopamine(PDA)containing lysoz...In this work,a novel coating with a non-antibiotic agent for inhibiting Gram-positive bacteria and promoting osteogenesis was prepared on zinc-aluminium alloy(ZA6-1)via mussel mimetic polydopamine(PDA)containing lysozyme(LYS)and parathyroid hormone(PTH).The results indicate that as-deposited coatings can efficiently decrease the degradation rate of ZA6-1 from 0.52 to 0.16 mm/year,and the addition of LYS weakens the coating resistance,while the addition of PTH enhances the coating resis-tance.In spite that no obvious inhibition of Escherichia coli is observed,the coated zinc alloys show good in vitro antibacterial performance against Staphylococcus aureus.Compared with ZA6-1 zinc alloys,the increase of antibacterial efficacy reaches 86.9%-90.1%.Furthermore,the lower hydrophilicity(26.4°),higher osteoblast cell viability(>100%),good osteoblast cell morphology and better osteoblast cell differentiation(ALP=107.7%)for PDA-LYS/PTH coated samples support that as-prepared coating is promising for modifying biodegradable zinc implants.展开更多
基金National Natural Science Foundation of China,Grant/Award Number:52271250Venture and Innovation Support Program for Chongqing Overseas Returnees,Grant/Award Number:cx2021106Natural Science Foundation of Chongqing Municipality,Grant/Award Number:CSTB2023NSCQ-MSX0977。
文摘In this work,a novel coating with a non-antibiotic agent for inhibiting Gram-positive bacteria and promoting osteogenesis was prepared on zinc-aluminium alloy(ZA6-1)via mussel mimetic polydopamine(PDA)containing lysozyme(LYS)and parathyroid hormone(PTH).The results indicate that as-deposited coatings can efficiently decrease the degradation rate of ZA6-1 from 0.52 to 0.16 mm/year,and the addition of LYS weakens the coating resistance,while the addition of PTH enhances the coating resis-tance.In spite that no obvious inhibition of Escherichia coli is observed,the coated zinc alloys show good in vitro antibacterial performance against Staphylococcus aureus.Compared with ZA6-1 zinc alloys,the increase of antibacterial efficacy reaches 86.9%-90.1%.Furthermore,the lower hydrophilicity(26.4°),higher osteoblast cell viability(>100%),good osteoblast cell morphology and better osteoblast cell differentiation(ALP=107.7%)for PDA-LYS/PTH coated samples support that as-prepared coating is promising for modifying biodegradable zinc implants.