The grain refinement behavior of Si-3 P,Si-25 Mn-10 P,and Al-10 Si-2 Fe-3 P master alloys on hypereutectic Al-24 Si alloy was studied.Microstructure analysis indicates that the P-containing compounds in the three mast...The grain refinement behavior of Si-3 P,Si-25 Mn-10 P,and Al-10 Si-2 Fe-3 P master alloys on hypereutectic Al-24 Si alloy was studied.Microstructure analysis indicates that the P-containing compounds in the three master alloys are Si P,Mn P,and Al P,respectively.The coarse flower-like primary silicon in the Al-24 Si alloy transforms into smaller,well-distributed blocks with the addition of various master alloys.When pouring at 840°C,the average grain size of the primary silicon refined by Si-25 Mn-10 P master alloy with a holding time of 30 min is about 18μm,which is significantly smaller than those refined by Si-3 P and Al-10 Si-2 Fe-3 P master alloys.The grain size shows an increasing trend when the holding time is further prolonged.Higher holding temperature has a positive effect on the grain refinement of Si-25 Mn-10 P master alloy.The grain refinement mechanism of the three master alloys was also discussed.展开更多
基金the support of the National Natural Science Foundation of China(51974057 and 5174057)the Open Project of State Key Laboratory of Advanced Special Steel,Shanghai Key Laboratory of Advanced Ferrometallurgy,Shanghai University(SKLASS 2019-19)the Science and Technology Commission of Shanghai Municipality(No.19DZ2270200)。
文摘The grain refinement behavior of Si-3 P,Si-25 Mn-10 P,and Al-10 Si-2 Fe-3 P master alloys on hypereutectic Al-24 Si alloy was studied.Microstructure analysis indicates that the P-containing compounds in the three master alloys are Si P,Mn P,and Al P,respectively.The coarse flower-like primary silicon in the Al-24 Si alloy transforms into smaller,well-distributed blocks with the addition of various master alloys.When pouring at 840°C,the average grain size of the primary silicon refined by Si-25 Mn-10 P master alloy with a holding time of 30 min is about 18μm,which is significantly smaller than those refined by Si-3 P and Al-10 Si-2 Fe-3 P master alloys.The grain size shows an increasing trend when the holding time is further prolonged.Higher holding temperature has a positive effect on the grain refinement of Si-25 Mn-10 P master alloy.The grain refinement mechanism of the three master alloys was also discussed.