Ni-W-TiC composite coatings were prepared via electrodeposition technique by dispersing the different amount of TiC particles into the plating bath.The Ni-W and Ni-W-TiC composite coatings containing different concent...Ni-W-TiC composite coatings were prepared via electrodeposition technique by dispersing the different amount of TiC particles into the plating bath.The Ni-W and Ni-W-TiC composite coatings containing different concentrations of TiC particles were characterized by using the scanning electron microscope,X-ray diffraction technique,Vickers microhardness test,surface roughness test,and tribology test.The results show that the Ni-W coatings containing reinforced TiC particles have shown a typical FCC Ni-W crystal structure with significantly higher Vickers microhardness.The amount of dispersed TiC particles into the plating bath considerably affected codeposition weight percent of TiC into the Ni-W matrix,as revealed by the EDS analysis.Ni-W-TiC samples demonstrated the decreased abrasive wear as compared to Ni-W coating and no characteristic features observed for the adhesive wear.Similarly,an improvement in coefficient of friction was observed in Ni-W-TiC composite coating as compared to Ni-W coating.展开更多
Optical properties of hot pressed Sialon ceramics doped with different rare earth oxides（REOs） i.e. Eu2O3, Gd2O3, and Pr2O3 were investigated. The α-Sialon phase was the main phase obtained after sintering as obser...Optical properties of hot pressed Sialon ceramics doped with different rare earth oxides（REOs） i.e. Eu2O3, Gd2O3, and Pr2O3 were investigated. The α-Sialon phase was the main phase obtained after sintering as observed by X-ray diffraction（XRD）. The transparency of different samples of varying thickness measured from UV to IR region revealed that the samples were translucent in the visible region while transparent in IR region. The thin samples of 150 μm thickness had transmittance as high as 30% in the visible region. The luminescence was observed in transmittance mode to investigate the effect of sample thickness on luminescence intensity. We observed blue, yellow and red emissions in Sialon doped with Gd2O3, Eu2O3, and Pr2O3, respectively. The excitation wavelength for Gd2O3 and Pr2O3 doped samples were in UV region i.e. 280 and 270 nm, respectively, whereas, for Eu2O3 doped samples was in the blue region（460 nm）. The Eu2O3 doped Sialon having 300 μm thickness showed better white light extraction as coupled with blue LED. Moreover, the fabricated phosphor samples exhibited high hardness around 20 GPa and fracture toughness above 5 MPa·m1/2.展开更多
基金This research was supported by the“International standardization of nickel-phosphorous ceramics electroless composite plating for industrial use”program through the “Korea Evaluation Institute of Industrial Technology”of Korea funded by the Ministry of Science,ICT and Future planning(Grant No.10080067)。
文摘Ni-W-TiC composite coatings were prepared via electrodeposition technique by dispersing the different amount of TiC particles into the plating bath.The Ni-W and Ni-W-TiC composite coatings containing different concentrations of TiC particles were characterized by using the scanning electron microscope,X-ray diffraction technique,Vickers microhardness test,surface roughness test,and tribology test.The results show that the Ni-W coatings containing reinforced TiC particles have shown a typical FCC Ni-W crystal structure with significantly higher Vickers microhardness.The amount of dispersed TiC particles into the plating bath considerably affected codeposition weight percent of TiC into the Ni-W matrix,as revealed by the EDS analysis.Ni-W-TiC samples demonstrated the decreased abrasive wear as compared to Ni-W coating and no characteristic features observed for the adhesive wear.Similarly,an improvement in coefficient of friction was observed in Ni-W-TiC composite coating as compared to Ni-W coating.
基金supported by Global Research Laboratory(GRL)Program of the National Research Foundation of Korea(NRF)funded by Ministry of Education,Science and Technology(MEST),Republic of Korea(2010-00339)
文摘Optical properties of hot pressed Sialon ceramics doped with different rare earth oxides（REOs） i.e. Eu2O3, Gd2O3, and Pr2O3 were investigated. The α-Sialon phase was the main phase obtained after sintering as observed by X-ray diffraction（XRD）. The transparency of different samples of varying thickness measured from UV to IR region revealed that the samples were translucent in the visible region while transparent in IR region. The thin samples of 150 μm thickness had transmittance as high as 30% in the visible region. The luminescence was observed in transmittance mode to investigate the effect of sample thickness on luminescence intensity. We observed blue, yellow and red emissions in Sialon doped with Gd2O3, Eu2O3, and Pr2O3, respectively. The excitation wavelength for Gd2O3 and Pr2O3 doped samples were in UV region i.e. 280 and 270 nm, respectively, whereas, for Eu2O3 doped samples was in the blue region（460 nm）. The Eu2O3 doped Sialon having 300 μm thickness showed better white light extraction as coupled with blue LED. Moreover, the fabricated phosphor samples exhibited high hardness around 20 GPa and fracture toughness above 5 MPa·m1/2.