Microstructure,phase composition and wear resistance of low valence electron concentration Al_(x)CoCrFeNiSi high-entropy alloys prepared by vacuum arc melting

The low valence electron concentration(VEC)Al_(x)CoCrFeNiSi(x=0.5,1.0,1.5 and 2.0)high-entropy alloys(HEAs)were designed by the fundamental properties of the constituent elements and prepared by vacuum arc melting method.The effects of Al addition on the crystal structure and microstructure were investigated.The microhardness and wear property were also researched.The results showed that the microstructure transformed from dendritic crystal to equiaxed crystal.It was found that FCC phase gradually decreased with the increasing Al content and disappeared until in a composition of 1.0 in Al_(x)CoCrFeNiSi HEAs.Little FCC phase was found with continuously adding Al,while the phase fraction of BCC increased from 85.0% to 91.8%,and VEC decreased from 7.00 to 6.14.The microhardness was increased gradually from 598 up to 909 HV with addition of Al from 0.5 to 2.0.It was the same of the compressive strength results,which improved from 1200 to 1920 MPa.The wear coefficient and mass loss were in line with mechanical properties evolution,which was attributed to the microstructure transformation into equiaxed crystal and the increase in BCC phase.

Influence of laser re-melting and vacuum heat treatment on plasma-sprayed FeCoCrNiAl alloy coatings

FeCoCrNiAl high entropy alloy coatings were prepared by supersonic air-plasma spraying.The coatings were post-treated by vacuum heat treatment at 600 and 900°C,and laser re-melting with 300 W,respectively,to study the influence of different treatments on the structure and properties of the coatings.The phase constitution,microstructure and microhardness of the coatings after treatments were investigated using X-ray diffraction,scanning electron microscopy and energy dispersive spectrometry.Results showed that the as-sprayed coatings consisted of pure metal and Fe-Cr.The AlNi;phase was obtained after the vacuum heat treatment process.A body-centered cubic structure with less AlNi;could be found in the coating after the laser re-melting process.The average hardness values of the as-sprayed coating and the coatings with two different temperature vacuum heat treatments and with laser re-melting were 177,227,266 and 682 HV,respectively.This suggests that the vacuum heat treatment promoted the alloying process of the coatings,and contributed to the enhancement of the coating wear resistance.The laser re-melted coating showed the best wear resistance.