Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work,...Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work, the limestone was modified with palygorskite to reduce sintering phenomenon between the absorbent particles during the CCS process and the carbonation rate of the limestone can be enhanced effectively. Palygorskite is a natural mineral with nano-fibrous structure which can reduce the mutual contact of limestone particles during the CCS process. The results were detected by TGA, SEM, MIP, FTIR and particle size analyzer respectively. The best CO_2 capture performance of modified absorbent was 13.11% improvement with only 5 wt% palygorskite added during the CCS process after 15 cycles compared with natural absorbent. It was found that excellent microscopic structures of absorbent modified with palygorskite was created, and the surface sintering was postponed leading to CO_2 capture performance enhanced under the same conditions.展开更多
基金Supported by the National Natural Science Foundation of China(51274159)Special Funds for The Major Science and Technology Innovation of Shaanxi Province(2012zkc06-2)
文摘Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work, the limestone was modified with palygorskite to reduce sintering phenomenon between the absorbent particles during the CCS process and the carbonation rate of the limestone can be enhanced effectively. Palygorskite is a natural mineral with nano-fibrous structure which can reduce the mutual contact of limestone particles during the CCS process. The results were detected by TGA, SEM, MIP, FTIR and particle size analyzer respectively. The best CO_2 capture performance of modified absorbent was 13.11% improvement with only 5 wt% palygorskite added during the CCS process after 15 cycles compared with natural absorbent. It was found that excellent microscopic structures of absorbent modified with palygorskite was created, and the surface sintering was postponed leading to CO_2 capture performance enhanced under the same conditions.