A series of linear poly(ethylene oxide)-b-poly(4-vinylbenzyl chloride)-b-poly(4-tert-butylstyrene)(PEO_(113)-b-PVBC_(130)-b-Pt BS_(x)or E_(113)V_(130)T_(x))triblock terpolymers with various lengths x(=20,33,66,104,215...A series of linear poly(ethylene oxide)-b-poly(4-vinylbenzyl chloride)-b-poly(4-tert-butylstyrene)(PEO_(113)-b-PVBC_(130)-b-Pt BS_(x)or E_(113)V_(130)T_(x))triblock terpolymers with various lengths x(=20,33,66,104,215)of Pt BS block were synthesized via a two-step reversible addition-fragmentation chain transfer(RAFT)polymerization.The E_(113)V_(130)T_(x)triblock terpolymers were non-crystalline because the PVBC and Pt BS blocks strongly hindered the crystallization of PEO block.The effects of Pt BS block length x on the phase structures of E_(113)V_(130)T_(x)triblock terpolymers were investigated by combined techniques of small-angle X-ray scattering(SAXS)and transmission electron microscopy(TEM).It was found that with increasing x from20 to 215,the phase structure of E_(113)V_(130)T_(x)triblock terpolymers became more ordered and changed from disordered structure,hexagonally-packed cylinder(HEX),hexagonally perforated layer(HPL),to lamellar(LAM)phase structures.Temperature-variable SAXS measurements showed that the HEX,HPL and LAM phase structures obtained for E_(113)V_(130)T_(66),E_(113)V_(130)T_(104)and E_(113)V_(130)T_(215)by thermal annealing,respectively,were thermodynamically stable in the temperature range of 30-170℃.展开更多
基金the National Natural Science Foundation of China(Nos.21875214,21674097 and 21774111)for financial support。
文摘A series of linear poly(ethylene oxide)-b-poly(4-vinylbenzyl chloride)-b-poly(4-tert-butylstyrene)(PEO_(113)-b-PVBC_(130)-b-Pt BS_(x)or E_(113)V_(130)T_(x))triblock terpolymers with various lengths x(=20,33,66,104,215)of Pt BS block were synthesized via a two-step reversible addition-fragmentation chain transfer(RAFT)polymerization.The E_(113)V_(130)T_(x)triblock terpolymers were non-crystalline because the PVBC and Pt BS blocks strongly hindered the crystallization of PEO block.The effects of Pt BS block length x on the phase structures of E_(113)V_(130)T_(x)triblock terpolymers were investigated by combined techniques of small-angle X-ray scattering(SAXS)and transmission electron microscopy(TEM).It was found that with increasing x from20 to 215,the phase structure of E_(113)V_(130)T_(x)triblock terpolymers became more ordered and changed from disordered structure,hexagonally-packed cylinder(HEX),hexagonally perforated layer(HPL),to lamellar(LAM)phase structures.Temperature-variable SAXS measurements showed that the HEX,HPL and LAM phase structures obtained for E_(113)V_(130)T_(66),E_(113)V_(130)T_(104)and E_(113)V_(130)T_(215)by thermal annealing,respectively,were thermodynamically stable in the temperature range of 30-170℃.