Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimet...Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimethylsiloxane(PVDMS)was formed on the surface of porous PVDF hollow fibers.The structural parameters of PVDFsubstrate membrane were estimated by gas permeation test.Using N_2/O_2 as the medium,the separation properties ofPVDMS-PVDF composite hollow fiber membranes were also evaluated experimentally.The experimental data of bothpermeability and selectivity are in good agreement with the theoretical results predicted by the presented pore-distributionmodel.In order to obtain the compact composite membrane free of defects by the dip-coating technique,the thickness ofPVDMS skin must be higher than 5 μm.展开更多
基金This work was supported by the National Natural Science Foundation of China(No.20076025).
文摘Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimethylsiloxane(PVDMS)was formed on the surface of porous PVDF hollow fibers.The structural parameters of PVDFsubstrate membrane were estimated by gas permeation test.Using N_2/O_2 as the medium,the separation properties ofPVDMS-PVDF composite hollow fiber membranes were also evaluated experimentally.The experimental data of bothpermeability and selectivity are in good agreement with the theoretical results predicted by the presented pore-distributionmodel.In order to obtain the compact composite membrane free of defects by the dip-coating technique,the thickness ofPVDMS skin must be higher than 5 μm.